The behavior of luminescence spectra and structural defects in single crystal Czochralski silicon after erbium implantation at 1 MeV energy and 1×1013 cm−2 dose with subsequent annealing at 1100 °C for 0.25–3 h in an argon or chlorine-containing ambience was studied by photoluminescence (PL), transmission electron microscopy, and chemical etching/Nomarski microscopy. We have found that annealing in the chlorine-containing ambience gives rise to dislocation loops and pure edge dislocations with dominant dislocation-related lines in the PL spectrum. Pure edge dislocations are responsible for the appearance of the lines. The Er-related lines due to the intra-4f shell transitions in the rare-earth ions dominate in the PL spectra and no structural defects are observed after annealing in argon. The observed differences in the optical and structural properties of Si:Er are associated with intrinsic point defects generated during the implantation and annealing.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.