Особенности фазообразования TbBO-=SUB=-3-=/SUB=- при изотермических отжигах

Abstract

Detailed X-ray studies of changes in the structure of terbium orthoborate TbBO_3 in the course of successive high-temperature isothermal annealing of the initial mixture in the form of an amorphous precursor and in the form of a homogenized mixture of microcrystalline Tb_7O_12 and B_2O_3 powders have been carried out. It is shown that the formation of TbBO_3 crystals in both cases occurs through the formation of intermediate two-phase states. Particularly, the triclinic high-temperature ν-TbBO_3 phase is formed already at the first crystallization stages (about 600°C) almost simultaneously with the equilibrium vaterite modification of TbBO_3 (sp. gr. P 63/ mmc ) during low-temperature annealing of an amorphous precursor, which transforms into the vaterite modification at an annealing temperature of 850°C. The phase of monoclinic terbium trioxoborate TbB_3O_6 is formed at the first stages of phase formation (about 800°C) almost simultaneously with the vaterite phase when the feedstock is annealed in the form of a homogenized mixture of microcrystalline Tb_7O_12 and B_2O_3 powders. It also transforms into the vaterite modification at an annealing temperature of 950°, which is preserved up to the highest annealing temperatures in the experiment (1200°C). A hypothetical explanation of the formation of such two-phase states during low-temperature annealing of the feedstock and their disappearance at higher annealing temperatures is proposed.

Тетрагональные нанокристаллические фазы в оксидах Re-=SUB=-2-=/SUB=-O-=SUB=-3-=/SUB=-

“…Нами ранее были проведены детальные структурные исследования ряда редкоземельных оксидных соединений, синтезированных из аморфного прекурсорного состояния [14][15][16][17][18][19][20][21][22][23][24][25][26][27][28]. Было показано, что их структура сильно зависит от размера кристаллитов.…”

“…Было показано, что их структура сильно зависит от размера кристаллитов. Так, для соединений LuBO 3 , Eu 2 (MoO 4 ) 3 , ScBO 3 и TbBO 3 [14][15][16], получаемых из аморфных прекурсоров, осуществляются циклические перестройки структуры с ростом размера кристаллитов. В этих соединениях при нагреве прекурсора первой кристаллизуется не равновесная для этой температуры, а высокотемпературная фаза.…”