Untersuchung von Säureinhibitoren hinsichtlich ihrer Wirkung gegenüber H‐induzierter Korrosion

Schlerkmann, H.; Schwenk, W.

doi:10.1002/maco.19840351003

Cited by 4 publications

(1 citation statement)

References 2 publications

Supporting

Mentioning

Contrasting

Order By: Relevance

“…Laboratory tests of ten commercially available substances used for the inhibition of acids did not show any correlation between the inhibiting effect for acid corrosion and for hydrogen absorption [5]. The results demonstrate, that the degree of reduction in iron dissolution is an unsuitable criterion for estimating the inhibition efficiency of hydrogen absorption.…”

Section: Inhibitorsmentioning

confidence: 81%

The influence of long term use of inhibitors in hydrochloric acid pickling baths on hydrogen induced stress corrosion cracking

Feser

Friedrich

Scheide

2002

Materials and Corrosion

View full text Add to dashboard Cite

Section: Inhibitorsmentioning

confidence: 81%

The influence of long term use of inhibitors in hydrochloric acid pickling baths on hydrogen induced stress corrosion cracking

Feser

Friedrich

Scheide

2002

Materials and Corrosion

View full text Add to dashboard Cite

Korrelationsbetrachtungen zum Einfluß von Säureinhibitoren auf die Metallauflösungsgeschwindigkeit und die Kinetik der Wasserstoffabsorption

Schlerkmann

Schmitt

1985

Materials & Corrosion

View full text Add to dashboard Cite

Durch weiterc Auswertung von Literaturdaten uber die Inhibitorwirkung von 53 quartaren Ammoniumsalzen, 13 aliphatischen und aromatischen Aldehyden sowie 12 aliphatischen und aromatischen Ketonen auf die Metallauflosungsgeschwindigkeit und Wasserstoffpermeationsstrome bei Stahl in H,S-freier und H,S-gesattigter 16%iger Salzsaure bei Raumtemperatur wird rnit Hilfe von Rang-Korrelationskoeffizientenbetrachtungen gezeigt, daR bei keinem Vertreter dieser Stoffklassen in keiner der betrachteten Medienarten eine Korrelation zwischen der Inhibition der Metallauflosungsrate und der Hemmung der Wasserstoffabsorption im Metall besteht. Es existiert aucb keine Korrelation zwischen der AntipromotodPromotor-Wirksamkeit bei freier Korrosion und bei kathodischer Polarisation in H2Sfreier und H,S-gesattigter Saure. Fragen der H-Absorption sind daher im Einzelfall unter praxisnahen Bedingungen zu prufcn.Evaluating literature data on the impact of 53 quarternary ammonium salts, 13 aliphatic and aromatic aldehydes and 12 aliphatic and aromatic ketones on the inhibition of the rate of metal dissolution and the hydrogen permeation currents at steel in H,S-free and H2Ssaturated 16% hydrochloric acid at ambient temperature, it is dcmonstrated by rank correlation considerations that there is no correlation between activity in blocking thc metal dissolution rate and efficiency in decreasing the hydrogen absorption rate of the metal. Furthermore, there is no correlation between antipromotoripromotor-efficiency at the tree corrosion potential and at cathodic polarization in H,S-free and H2S-saturated acid. Problems of H-absorption therefore have to be investigated for any particular case under conditions as close to the practice as possible.

show abstract

Einflüsse von Legierungselementen auf die Korrosion und Wasserstoffaufnahme von Eisen in Schwefelsäure – Teil I: Permeation, Diffusion und Löslichkeit von Wasserstoff in binären Eisenlegierungen

Riecke

Johnen

Grabke

1985

Materials & Corrosion

View full text Add to dashboard Cite

rer. nat. Hans-Jurgen Engell zurn 60. Geburtstag gewidmet E. Riecke, 6. Johnen und H. J. Grabke' Die Einflusse der in Stahlen ublichen Begleit-und Legierungselemente C, S , P, Mn, Si, Cr, Ni, Sn und Cu auf die Aufnahme und Permeation von Wasserstoff durch Eisen wurden mit Hilfe der elektrochemischen Permeationsmethode an binaren Eisenlegierungen untersucht. Zur Beschreibung des Einflusses der Legierungszusatze auf die Wasserstoffaktivitat an der Metalloberflache sowie den Wasserstofftransport im Volumen wurden der Permeationskoeffizient, der Diffusionskoeffizient und die Loslichkeit des Wasserstoffs fur Temperaturen zwischen 10 und 80°C bestimmt. Die stationare Wasserstoffpermeation wird allein durch Si und Cr starker gehemmt. Si erniedrigt vor allem die Loslichkeit des Wasserstoffs in Eisen und hemmt weniger die Diffusion. Cr verursacht im Eisengitter Platze hoher Bindungsenergie (-58 kJ/mol) fiir Wasserstoff und erniedrigt damit dessen Beweglichkeit . Die Gesamtwasserstoffkonzentration wird durch Cr erhoht. Permeationsmessungen an handelsublichen Stahlen zeigen vor allem den Si-Einflul3.

show abstract

Untersuchung von Säureinhibitoren hinsichtlich ihrer Wirkung gegenüber H‐induzierter Korrosion

Cited by 4 publications

References 2 publications

The influence of long term use of inhibitors in hydrochloric acid pickling baths on hydrogen induced stress corrosion cracking

The influence of long term use of inhibitors in hydrochloric acid pickling baths on hydrogen induced stress corrosion cracking

Korrelationsbetrachtungen zum Einfluß von Säureinhibitoren auf die Metallauflösungsgeschwindigkeit und die Kinetik der Wasserstoffabsorption

Einflüsse von Legierungselementen auf die Korrosion und Wasserstoffaufnahme von Eisen in Schwefelsäure – Teil I: Permeation, Diffusion und Löslichkeit von Wasserstoff in binären Eisenlegierungen