Abstract:The effect of a chromium (Cr) transition layer on the hot-salt corrosion behavior of an AlSi alloy coating was studied. Hot-salt corrosion experiments were performed at 650 °C and corrosion kinetic curves were plotted. The weight gain of the AlSi-coated samples increased to 0.89 mg/cm2 at 100 h and then decreased steadily to 0.77 mg/cm2 at 200 h. The weight of the AlSi-coated samples with the addition of a Cr transition layer increased immediately to 0.79 mg/cm2 at 20 h and then gradually increased to 0.85 mg/… Show more
Set email alert for when this publication receives citations?
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.