This study investigated the potential effect of vacuum annealing on the microstructure and hot salt corrosion behavior of CoNiCrAlY/YSZ/LaMgAl11O19 (LMA) double-ceramic coatings. A hot-salt corrosion test revealed that sprayed coatings exhibited an unsatisfactory anti-corrosion performance, and the LMA layer underwent severe fracture and corrosion degradation. Vacuum annealing induced a prominent recrystallization of the amorphous phase in LMA layer, triggering severe volume shrinkage and microcrack initiation. The recrystallization and volume shrinkage of the LMA layer were aggravated by an increase in the annealing temperature. The annealed coating with a higher fraction of the LaMA phase showed superior resistance to hot-salt corrosion. However, the salt mixture diffused simultaneously along the microcracks and eventually eroded into the YSZ layer. These results confirmed that vacuum annealing significantly enhanced the hot-salt corrosion resistance of the LMA layer. However, it deteriorated the barrier effect of the salt mixture through microcrack formation.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.