Unconfined Compressive Strength of Aqueous Polymer-Modified Saline Soil

The reinforcement and durability of loess are of great importance for road performance. In this study, a self-designed grouting system and newly permeable polymers were adopted to investigate the mechanical properties and durability of solidified loess (SL), considering different dry densities and water contents. The unconfined compression test and piezocone penetration (CPTU) test were used to examine the mechanical properties. The mechanism of the loess solidified by permeable polymer was analyzed from the micro-level by SEM, MIP, and XRD tests. The test results show that the effect of polymer grouting is obvious, the unconfined compressive strength (UCS) of the SL after grouting is as high as 3.05–5.42 MPa; it is 11.83–20.99 times that of unsolidified loess (UL). The UCS of the SL after grouting is inversely proportional to the dry densities and water contents. After 56 days of immersion, the SL still shows a high compressive strength. The additional erosion of the SL was not caused by the salt solution; the durability is significantly better than that of cement mixing soil. The sensitivity of various factors on the UCS of the SL are service environment > water content > dry density. The SEM tests clearly show that the gel formed by the reaction of the polymer with water on the surface of soil particles makes the bond of soil particles tighter. It can be observed from the MIP test that the cumulative mercury of SL was 0.115 mL/g, which was 33.72% of UL (0.341 mL/g), and the cumulative mercury of SL after immersion in water and salt solutions was 0.183 mL/g and 0.175 mL/g, which was 53.7% and 51.3% of UL (0.341 mL/g), respectively. The XRD results show that there are no other new mineral components produced after grouting and the spacing between crystalline planes decreases, which proves that permeable polymer grouting makes the soil denser and does not erode the soil particles.

show abstract

“…This is consistent with the results observed by the SEM test. This conclusion is also consistent with Zhu’s findings [ 48 ].…”

Section: Resultssupporting

confidence: 93%

Study on Mechanical Properties of Permeable Polymer Treated Loess

et al. 2022

View full text Add to dashboard Cite

show abstract

“…Both actions by the polymer increased the ability of the soil particles to connect with each other; therefore, the permeability of the soil decreased; water affects the strength of the soil in a much reduced manner, and the compactness of the soil increases. As a result, the strength of the soil is significantly improved [17,26].…”

Section: Microscopic Mechanism Of Silt Solidification Induced By the Polymermentioning

confidence: 99%

Strength and Solidification Mechanism of Silt Solidified by Polyurethane

Wang

Xia

et al. 2020

Advances in Civil Engineering

View full text Add to dashboard Cite

To determine the mechanism and strength characteristics of solidification of silt by a permeable polyurethane grouting material, the effects of polymer content, soil moisture, and immersion time on the unconfined compressive strength (UCS) of the silt have been studied. The results showed that the permeable polymer grouting material can significantly improve the performance of silt: (1) A higher amount of polymer produced a greater strength in the solidified soil. (2) The strength of the solidified soil increased as the immersion time was increased. (3) Moisture in the soil was not conducive to improving the strength of the solidified soil. The X-ray diffraction (XRD) and energy-dispersive spectroscopy (EDS) have proven that polyurethane does not react with the silt, but they could improve the strength of the silt through physical action. Mercury intrusion porosimetry (MIP) and scanning electron microscopy (SEM) were performed to find that polymers can reduce soil porosity, and the addition of polyurethane improved the strength of the silt mainly through adhesion, wrapping, filling, and bridging.

show abstract