Thermocycling Effects on Shear Bond Strength of a Self-Etching Primer

Abstract

The results of this study indicate that the SEP (Transbond Plus) provides clinically acceptable bond strength values compared with the conventional method after thermocycling.

Comparison of enamel-bracket bond strength using direct- and indirect-bonding techniques with a self-etching ion releasing S-PRG filler

“…This difference may explain why the penetration of the self-etching primer into the enamel was lower than with 37% phosphoric acid 15) . Elekdag-Turk et al 33) not observed significant decrease in the mean SBS of systems that had been prepared with phosphoric acid etching after 2,000 and 5,000 thermal cycles, whereas systems that had been prepared with self-etching primer showed a significant decrease of the mean SBS value after 2,000 thermal cycles. However, Daub et al 41) reported a significant decrease in the mean SBS of metal brackets, directly and indirectly bonded with phosphoric acid and TX adhesive, after only 500 thermal cycles.…”

“…BO displays a lower pH value and milder self-etching ability compared to TP. The lower SBS of BO, compared to TP and TX 33) , may arise from the reduced penetration of the adhesive resin into the enamel surface. Indeed, lower porosity in BO systems has been observed via SEM micrographs of untreated enamel surfaces, phosphoric acid-etched surfaces, and self-etched surfaces (TP and BO) 31,32) .…”

“…Numerous studies have investigated the strength of self-etching primer systems 15,18,19,[23][24][25][26][27][28][29][30][31][32][33] . Most of these studies demonstrated that self-etching systems have significantly lower SBS values than conventional acidetching systems 18,24,26,34,35) .…”

Resistencia al cizallamiento e indice adhesivo remanente (ARI) de dos cementos ortodónticos fotopolimerizables antes y después del termociclado

“…(4)(5)(6) Fue así como se creó el índice adhesivo remanente (ARI), que ha sido ampliamente utilizado en los estudios con la finalidad de evaluar la cantidad de cemento restante después de retirar un bracket. (1,(3)(4)(5)(6)(7)(8)(9)(10) Dentro de los cementos ortodónticos actuales se encuentra el Transbond TM XT, el cual es considerado como "gold standard" por su consistencia ideal, capacidad de fotocurado y adhesión superior entre el bracket y el diente. (11) Sus componentes están conformados por primer y cemento.…”

“…(12) diferentes temperaturas en la cavidad oral. Por ese motivo, distintos autores (7)(8)(9)(13)(14)(15)(16) recomiendan realizar en sus estudios el termociclado, un proceso in vitro que consiste en exponer las muestras a temperaturas extremas para simular las condiciones de la cavidad oral y envejecer la muestra. (8,15) Por ello, el propósito de este estudio fue comparar in vitro, en función al termociclado, la resistencia al cizallamiento y el índice adhesivo remanente (ARI) utilizando los cementos Transbond TM XT (3M Unitek, Monrovia, California, USA) y OrthoCem (FGM, Joinville, Brazil) en dientes de bovino.…”