Tailoring the Mesoscopic TiO2 Layer: Concomitant Parameters for Enabling High-Performance Perovskite Solar Cells

Abstract

Architectural control over the mesoporous TiO2 film, a common electron-transport layer for organic-inorganic hybrid perovskite solar cells, is conducted by employing sub-micron sized polystyrene beads as sacrificial template. Such tailored TiO2 layer is shown to induce asymmetric enhancement of light absorption notably in the long-wavelength region with red-shifted absorption onset of perovskite, leading to ~20% increase of photocurrent and ~10% increase of power conversion efficiency. This enhancement is likely to be originated from the enlarged CH3NH3PbI3(Cl) grains residing in the sub-micron pores rather than from the effect of reduced perovskite-TiO2 interfacial area, which is supported from optical bandgap change, haze transmission of incident light, and one-diode model parameters correlated with the internal surface area of microporous TiO2 layers. With the templating strategy suggested, the necessity of proper hole-blocking method is discussed to prevent any direct contact of the large perovskite grains infiltrated into the intended pores of TiO2 scaffold, further mitigating the interfacial recombination and leading to ~20% improvement in power conversion efficiency compared with the control device using conventional solution-processed hole blocking TiO2. Thereby, the imperatives that originate from the structural engineering of the electron-transport layer are discussed to understand the governing elements for the improved device performance.Electronic supplementary materialThe online version of this article (doi:10.1186/s11671-016-1809-7) contains supplementary material, which is available to authorized users.

Interfacial Modification of Mesoporous TiO2 Films with PbI2-Ethanolamine-Dimethyl Sulfoxide Solution for CsPbIBr2 Perovskite Solar Cells

“…No interface between CsPbIBr 2 and m-TiO 2 layers can be clearly distinguished. Combined with the conclusions of XRD, we can confirm that the abundant perovskite precursor solution diffuses into the m-TiO 2 film during the spin-coating process and generates CsPbIBr 2 to fill up the pores, which is conductive to the transportation and collection process for the carriers [ 38 , 39 ].…”

Bioinspired scaffolds that sequester lead ions in physically damaged high efficiency perovskite solar cells

“…The latter is a 73 meV red-shift due to replacing TiO 2 NPs with HAP NPs. This is likely due to the increased grain size 30 noted above. The red shift was also apparent from the PL spectra (see Fig.…”

Microstructural Evolution of Hybrid Perovskites Promoted by Chlorine and its Impact on the Performance of Solar Cell

“…Series and shunt resistances are extracted by fitting the light J-V curves to the ideal one-diode model (Fig. S 7) 34 , 35 . Series resistance from the 20-mol.-% MACl cell is much better (0.5 Ω·cm 2 ) than that of the stoichiometric-precursor-based cell (1.7 Ω·cm 2 ).…”