Synthesis of Graphene Oxide (GO) by Modified Hummers Method and Its Thermal Reduction to Obtain Reduced Graphene Oxide (rGO)*

Abstract

Over the span of years, improvements over various synthesis methods of graphene are constantly pursued to provide safer and more effective alternatives. Though the extraction of graphene through Hummers method is one of the oldest techniques yet it is one of the most suitable methods for the formation of bulk graphene. Graphene can be obtained in the form of reduced Graphite oxide, sometimes also referred as Graphene oxide. The effectiveness of this oxidation process can be evaluated by the magnitude of carbon/oxygen ratio of the obtained graphene. Here, graphene oxide (GO) was prepared by oxidizing the purified natural flake graphite (NFG) by a modified Hummers method. The attempts have been made to synthesize GO having few layers by using a modified Hummers method where the amount of NaNO 3 has been decreased, and the amount of KMnO 4 is increased. The reaction has been performed in a 9:1 (by volume) mixture of H 2 SO 4 /H 3 PO 4 . This modification is successful in increasing the reaction yield and reducing the toxic gas evolution while using a varied proportion of KMnO 4 and H 2 SO 4 as those required by Hummers method. A new component of K 2 S 2 O 8 has been introduced to the reaction system to maintain the pH value. Reduced graphene oxide (rGO) was thereafter extracted by thermal modification of GO. Here, GO has been used as a precursor for graphene synthesis by thermal reduction processes. The results of FTIR and Raman spectroscopy analysis show that the NFG when oxidized by strong oxidants like KMnO 4 and NaNO 3 , introduced oxygen atoms into the graphite layers and formed bonds like C=O, C-H, COOH and C-O-C with the carbon atoms in the graphite layers. The structure and morphology of both GO and rGO were analyzed using X-ray diffraction (XRD), scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HR-TEM), Fourier transform infrared spectroscopy (FTIR), ultraviolet-visible spectroscopy, Raman spectroscopy, Brunauer-Emmett-Teller (BET) surface area analysis and differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA).

Rational Construction of V2O5@rGO with Enhanced Pseudocapacitive Storage for High‐Performance Flexible Energy Storage Device

“…Synthesis of V 2 O 5 @rGO (VrG) : The preparation of graphene oxide (GO) was derived from improved Hummers methods . (36.4, 18.2 and 9.1) mg GO were dispersed in 30 ml ethanol under ultrasonic treatment for 30 min, then these GO dispersion solutions were injected respectively into the above dark red mixed solution with continuous stirring for 20 min at room temperature.…”

Green synthesis of silver nanoparticles using Eucalyptus comadulensis leaves extract and its immobilization on magnetic nanocomposite (GO‐Fe3O4/PAA/Ag) as a recoverable catalyst for degradation of organic dyes in water

“…Nanosheets of GO were synthesized with the modified Hummers' procedure . In a common procedure, a flask containing 250 ml of H 2 SO 4 was placed in an ice bath and 2.5 g of NaNO 3 and 5.0 g of graphite were added to it.…”

Silicon‐grafted Ag/AgX/rGO nanomaterials (X = Cl or Br) as dip‐photocatalysts for highly efficient p‐nitrophenol reduction and paracetamol production

“…Graphene oxide (GO) was prepared using a modified Hummer's method . In a typical procedure, H 2 SO 4 (150 ml) was added into a flask containing graphite (6 g) in an ice bath under stirring.…”