Spectroscopic and Diffractional Characteristics of Membranes and Polyamide 6/Regional Bentonite Clay Nanocomposites

Maia, Larissa Fernandes; Leite, Amanda Melissa Damião; Araújo, Edcleide Maria; Lira, Hélio Lucena; Paz, Renê Anísio da

doi:10.4028/www.scientific.net/msf.775-776.168

Cited by 10 publications

(15 citation statements)

References 12 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…21.8° of the crystalline plan (001), which can be attributed to phase γ (gamma) of PA6 36,37 . The addition of 10% w/w of CaCl 2 in the solution of membrane preparation did not cause significant changes with regard to the crystalline behavior and the main crystalline phase is α, as illustrated by the X-ray diffraction curve of pure PA6 membranes and their hybrids.…”

Section: Water Permeability and Oil Retentionmentioning

confidence: 99%

Hybrid Membranes of Polyamide Applied in Treatment of Waste Water

et al. 2017

View full text Add to dashboard Cite

In this work, it was prepared hybrid membranes of polyamide6 (PA6) with montmorillonite (MMT) and porogenic agent (CaCl 2 ). The hybrid membranes with CaCl 2 were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), scanning electron microscopy (SEM), porosimetry by mercury intrusion (PMI), flux measurements and rejection. By means of X-ray diffraction, it was revealed that the hybrid membranes with CaCl 2 have an exfoliated and/or partially exfoliated structure. For FTIR and DSC of hybrid membranes with CaCl 2 , it was found that the spectra and the crystalline melting temperature remained virtually unchanged compared to PA6 membrane. From the SEM images, it was observed that the addition of the MMT and the CaCl 2 in the membrane of PA6 caused an increase in the amount of pores the surface and cross section of these membranes. By PMI, it was observed that the presence of MMT and CaCl 2 in the membrane caused an increase in the average diameters of pores. The water-oil separation tests, indicated a significant reduction of oil in the permeate, allowing treatment of wastewater contaminated with oil.

show abstract

Section: Water Permeability and Oil Retentionmentioning

confidence: 99%

Hybrid Membranes of Polyamide Applied in Treatment of Waste Water

et al. 2017

View full text Add to dashboard Cite

show abstract

“…The addition of 1, 3, and 5% in weight of OMMT (Figure ) on the PA6 membrane caused a morphological modification on its surface, presenting a flat structure with greater number of pores, as well as, the formation of a pore structure of spherical shape, well distributed in the porous layer along its cross‐section …”

Section: Resultsmentioning

confidence: 53%

Hybrid Microporous Membranes Applied in Wastewater Treatment

Medeiros

Lima

et al. 2019

Macromolecular Symposia

View full text Add to dashboard Cite

In this work, membranes of pure polyamide 6 (PA6) and hybrids with 1, 3, and 5% in weight of organophilic montmorillonite (OMMT) clay in the form of thin porous films are obtained by the phase inversion technique. The membranes are characterized by X‐ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), scanning electron microscopy (SEM), mercury intrusion porosimetry (MIP), contact angle (CA), and flow measurements (FM). Through X‐ray diffraction, it is revealed that the hybrid membranes with OMMT have an exfoliated and/or partially exfoliated structure. From FTIR and DSC analyses of hybrid membranes with OMMT, it is found that the spectra and the crystalline melting temperature remained practically unchanged compared to PA6 membrane. From the SEM, it is verified that the addition of the clay caused an increase in the quantity and uniformity of pores distribution in the surface and cross section of these membranes. By MIP, it is observed that the presence of clay in the membrane caused an increase in the average pore diameters. By the contact angle, it is verified that the membrane with clay had a higher value of contact angle for the distilled water when compared to the angle obtained with the synthetic oil. The water flux of the membrane with clay is higher than that obtained by the membrane of pure PA6, due its surface structure with larger pore diameters, favoring its permeability. The obtained hybrid membrane presented adequate porosity morphology for wastewater treatment.

show abstract

“…Analisando a PA6 pura e seus híbridos, foi possível observar que a fase cristalina predominante é a alfa [24][25][26]29]. Além disso, foi constatada nas membranas com 3% e 5% de argila, a presença de um pico em aproximadamente 27°, referente ao elemento quartzo da argila.…”

Section: Figuraunclassified

“…A adição de 1%, 3% e 5% em peso de argila (Figura de 5 a 7) na membrana de PA6 provocou uma modificação morfológica na sua superfície, apresentando uma estrutura com poros mais abertos e uma maior quantidade deles, bem como, a formação de uma estrutura com poros interconectados de formato esférico e bem distribuídos provenientes da camada porosa mostrada ao longo de sua seção transversal [23][24][25][26].…”

Section: Figuraunclassified

“…As cargas minerais do tipo bentonita são facilmente encontradas na região da Paraíba. Elas vêm sendo utilizadas em nanocompósitos e apresentando resultados bastante promissores para aplicações em membranas híbridas; dessa forma, o estudo destas é interessante não só do ponto de vista tecnológico, mas também um incentivo para as indústrias locais [23][24][25][26][27].…”

Section: Introductionunclassified

See 1 more Smart Citation

Membranas microporosas híbridas assimétricas: influência da argila na morfologia das membranas

Medeiros¹,

Araújo²,

Lira³

et al. 2017

Matéria (Rio J.)

View full text Add to dashboard Cite

RESUMO Neste trabalho, foram obtidas membranas híbridas de poliamida6 (PA6) com 1%, 3% e 5% em peso de argila na forma de filmes finos por meio da técnica de inversão de fases. As membranas híbridas foram caracterizadas por difração de raios-X (XRD), espectroscopia na região do infravermelho com transformada de Fourier (FTIR), calorimetria exploratória diferencial (DSC), microscopia eletrônica de varredura (SEM), porosimetria por intrusão de mercúrio (MIP) e ângulo de contato. Por meio do XRD, foi possível perceber que as membranas híbridas sugerem uma estrutura esfoliada e/ou parcialmente esfoliada. Os espectros de FTIR das membranas híbridas permaneceram inalterados, exceto pelo aumento na intensidade dos picos em 800, 1033 e 1095 cm−1 provavelmente referente à camada octaédrica e a vibração do estiramento do grupo Si- O-Si da argila. Por DSC foi observado que praticamente não houve alteração da temperatura de fusão cristalina das membranas híbridas em relação à membrana de PA6 pura. A partir das fotomicrografias obtidas por SEM, foi ilustrada a obtenção de membranas microporosas assimétricas com a formação de uma pele filtrante e um suporte poroso ao longo da seção transversal. Além disso, a adição da argila provocou um aumento na quantidade e distribuição uniforme dos poros existentes na superfície e seção transversal destas membranas. Por MIP, observou-se que a presença da argila nas membranas ocasionou um aumento nos diâmetros médio dos poros. Por meio do ângulo de contato, verificou-se que as membranas híbridas apresentaram maiores ângulos de contato para a água destilada quando comparadas aos ângulos obtidos com o óleo sintético. As membranas híbridas obtidas apresentaram uma morfologia com porosidade adequada para aplicação em processos de microfiltração.

show abstract

Spectroscopic and Diffractional Characteristics of Membranes and Polyamide 6/Regional Bentonite Clay Nanocomposites

Cited by 10 publications

References 12 publications

Hybrid Membranes of Polyamide Applied in Treatment of Waste Water

Hybrid Membranes of Polyamide Applied in Treatment of Waste Water

Hybrid Microporous Membranes Applied in Wastewater Treatment

Membranas microporosas híbridas assimétricas: influência da argila na morfologia das membranas