Role of oxygen vacancies and In‐doping on the sensing performance of ZnO particles

Abstract

Pure and In‐doped ZnO particles with two morphologies: rods and platelets were synthesized using hydrothermal method and tested for gas sensing. The materials were characterized by X‐ray diffraction, scanning electron microscopy and Raman spectroscopy. Platelets were synthesized with zinc acetate and potassium hydroxide in a ratio 1:3, while rods were obtained for a ratio1:8. As‐synthesized particles do not exhibit any sensing response. The creation of oxygen vacancies, through thermal treatments under reducing atmosphere (Ar:H2), activate the sensing properties. The best sensitivity, upon exposure of CO and propane, was obtained on the In‐doped platelets with large ±(0001) surface area. The value of the contact barrier between particles after the thermal treatment is 164 µeV.

Técnicas de microscopía electrónica usadas en el estudio de nanopartículas

“…En las imágenes de las figuras 23c y 23d se muestran las distancias interplanares correspondientes en ambos tipos de partículas, los valores de la medición pertenecen al ZnO y se asigna a la familia de planos en la notación de índices de Miller. La aplicación de estas partículas puras y con dopantes en la detección de gases se señala en el artículo "Role of oxygen vacancies and in-doping on the sensing performance of ZnO particles" (Montes-Fonseca et al, 2017). Recientemente publicamos otras variantes en la morfología de estas partículas, en relación con su efectividad como material antifúngico: "Shape-dependent antifungal activity of ZnO particles against phytopathogenic fungi" (Pariona et al, 2020).…”