Impact of phenol film grammage on chosen mechanical properties of plywood. For the purpose of this research several plywood samples with a thickness of 15 mm were produced and coated, in industrial conditions, with 5 different variants of phenol films varying in terms of grammage (40/120 g/m2, 60/145 g/m2, 60/167 g/m2, 80/220 g/m2, 2 × 80/220 g/m2). Finished plywood was tested for abrasion resistance, MOR, MOE and density. It was concluded that higher grammage of phenol film increases wear resistance and final density of plywood. Plywood coated with two-layer phenol film with grammage of 80/220 g/m2 had 4 times higher rate of abrasion resistance in comparison with plywood coated with phenol film with surface density of 40/120 g/m2. Coating plywood surface with phenol films generally decreases MOR values, in comparison with uncoated plywood. In terms of MOE, there were no evidence of conclusive relation, despite statistically significant differences between each variant.