Abstract:The high-density (with the relative density up to 98,8 %) ultrahigh temperature ZrB2‒TaC‒SiC ceramic materials (UHTCs) were prepared by means of the hot Argon pressing 30 MPa at 2000 °C, and isothermal time 15 minutes. After this the phase composition, crystal lattice parameters, ultimate bending stress, Vickers hardness, and the cracking resistance were investigated. The maximum values of the bent stress, hardness, and cracking resistance were 440 MPa, 20 GPa and 5,3 MPa·m1/2respectively. It was shown that th… Show more
Set email alert for when this publication receives citations?
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.