Photoelectric Properties of Photoconducting Composites Based on Non-Photoconducting Polymers Doped by Triarylmethane and Xanthene Dyes

Abstract

The films of polymeric composites based on non-photoconducting polyvinyl alcohol and polystyrene doped by various concentration of xanthene and triarylmethane type dyes have been prepared. Their photophysical, electrical, and spectral properties have been investigated. It was shown, that all studied composite films exhibit photovoltaic properties and anomalous negative photoconductivity effect. The diffusion nature of observed photovoltaic effect was established. The features of photovoltaic effect and photoconductivity, as well as the possible negative photoconductivity mechanism are discussed.

The Effect of the Substituent Nature in the Azobenzene Chromophores on Diffraction Efficiency of Polarization Holograms

“…В образцах сэндвич-структуры измеряли: плотность темнового тока (jd) и фототока (jPH) в зависимости от величины и полярности электрического напряжения (U) (соответственно от величины напряженности Е = U/L электрического поля и направления силовых линий этого поля в образцах), приложенного к электрическим контактам [9], а также диэлектрические характеристики полученных ППК -величину тангенса угла диэлектрических потерь (tgδ) и электрической емкости (C) для частоты f = 200-10 3 Гц синусоидального переменного электрического напряжения с действующим значением 10 В без облучения и при облучении светом [10][11]. Из последних измерений рассчитывали величину ΔtgδPH = (tgδPH -tgδ0)/tgδ0 и ΔCPH = (CPH -C0)/C0, где tgδ0, C0 и tgδPH, CPH соответственно значения тангенса угла диэлектрических потерь и емкости до и после включе-ния света облучения.…”

“…Во всех исследованных ППК величина относительного изменения ΔtgδPH < 0, т.е. величина тангенса угла диэлектрических потерь tgδ, уменьшается при облучении (величина электрической емкости также незначительно уменьшается), что может свидетельствовать об уменьшении величины дипольного момента азохромофоров при облучении, либо также об уменьшении подвижности или концентрации свободных подвижных носителей тока в системе [10][11]15]. Результаты проведенных нами дополнительных исследований темновой электро-, а также фотопроводимости созданных ППК (в образцах сэндвич-структуры) свидетельствуют о том, что вплоть до напряженностей порядка Е ~ 3-4•10 7 В/м внешнего электрического поля (что в 6-7 раз превосходит величину напряженности электрических полей, используемых нами в фотодиэлектрических исследованиях) соответствующие величины фототоков во всех исследованных ППК не превосходят заметно уровня шумов, что говорит о практическом отсутствии влияния вклада процессов фотопроводимости за счет свободных фотогенерированных носителей заряда в объеме ППК на величину фотодиэлектрического эффекта в исследованных ППК.…”

Photoelectric properties of the photoconducting film composites based on ferrocenyl‐ and carbazolyl‐containing oligomer doped with polymethine dye

“…Following characteristics were measured in the samples: spectra of optical density (D) of the polymeric film composites films; electrical potential (V PH ) of the polymeric film composites films free surface or Ag‐electrode respectively to ITO electrode before illumination with light, its changes during (t) illumination from the side of transparent electroconducting ITO layer as well as after the light is ceased. Technique of measurement of the surface potential by dynamic probe (modified Kelvin technique ) was employed for determination of the photovoltaic characteristics in the samples with free surface of polymeric film composites films. This technique was chosen because it eliminates influence of contact potential difference appearing in the samples of sandwich structure with different electrodes on the photoprocesses in the polymeric film composites films.…”

“…Kinetics of V PH changes in the samples with free surface of the polymeric film composites films was registered by USB oscilloscope BM8020. Kinetics of photovoltaic response in the samples of sandwich structure was registered electrometrically by memory oscilloscope Tektronix TDS1001B . For the samples illumination semiconductor light diodes with irradiation maximums 420 nm (blue), 532 nm (green), 590 nm (yellow) and 630 nm (red) as well as white diode were used.…”

“…In the samples with free surface investigations of characteristics of the photovoltaic response V PH by Kelvin technique were carried out. The polymeric film composites samples were illuminated by respective light diodes in the active area of the probe from the side of glass substrate and transparent ITO electrode . Dielectric characteristics of polymeric film composites such as tangent of angle of dielectric losses (tg δ) at the frequency f = 1 kHz of sinusoidal alternating electric voltage without illumination and under illumination with light from absorption range of Dye1 were measured in the samples of sandwich structure .…”