Oxidation and electrical behavior of AISI 430 coated with cobalt spinels for SOFC interconnect applications

Ebrahimifar, Hadi; Zandrahimi, Morteza

doi:10.1016/j.surfcoat.2011.06.046

Cited by 51 publications

(17 citation statements)

References 47 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…In addition, the formation of interfacial defects, such as voids, cavities and spallation, is also an important factor that influences the stability of the SOFC stacks. 94,95 The scattering of the ASR data is observed for the uncoated sample after ∼120 hours of operation, which could be ascribed to the structural instability at the interface. 96 It was reported that the interfacial strength between the metallic interconnect and the oxide scale decreases with the growth of the chromia scale, and the thick scale readily causes spallation because of the increased thermal stress.…”

Section: Resultsmentioning

confidence: 99%

Highly Dense Mn-Co Spinel Coating for Protection of Metallic Interconnect of Solid Oxide Fuel Cells

Lee

Hong

Kim

et al. 2014

J. Electrochem. Soc.

View full text Add to dashboard Cite

The major degradation issues of solid oxide fuel cells (SOFC) are associated with the oxide scale growth and Cr evaporation of the metallic interconnect. To address these challenges, a highly dense spinel oxide coating was fabricated on a ferritic stainless steel interconnect using a cost-competitive ceramic processing route. The nano-scale Mn 1.5 Co 1.5 O 4 spinel powder was synthesized using a glycine-nitrate method, and the particle agglomerates were effectively disintegrated by a high-energy attrition milling process. The spinel protective coating, which was applied by screen printing, was sintered to a nearly full density, without causing damage to the metallic substrate, by a high-temperature annealing process in a reducing environment, followed by re-oxidation at a moderate temperature. The dense spinel coating remarkably reduced the growth rate of chromia scale and restrained the evaporation of chromium species, as verified by area specific resistance (ASR) measurements and analysis on chromium distribution over the cross-section. Strong adhesion between the coating and substrate was confirmed after 500-hour operation. The sintering mechanism involved in reduction-oxidation heat-treatment was studied based on dilatometry measurements and microstructural features. The implication of the ASR change and the chromium migration for stability of practical SOFC stacks was discussed in detail.

show abstract

Section: Resultsmentioning

confidence: 99%

Highly Dense Mn-Co Spinel Coating for Protection of Metallic Interconnect of Solid Oxide Fuel Cells

Lee

Hong

Kim

et al. 2014

J. Electrochem. Soc.

View full text Add to dashboard Cite

show abstract

“…Although various techniques have been developed to apply Mn-Co spinel coatings to ferritic stainless steels, the pack cementation method has not been used extensively to produce Mn-Co oxides for SOFC interconnect applications. Very little research has been done on the production of such coatings for SOFC interconnect applications [20][21][22].…”

Section: Introductionmentioning

confidence: 99%

Oxidation and Electrical Behavior of Mn-Co-Coated Crofer 22 APU Steel Produced by a Pack Cementation Method for SOFC Interconnect Applications

Ebrahimifar

Zandrahimi

2015

Oxid Met

Self Cite

View full text Add to dashboard Cite

An issue associated with chromia-scale formation on ferritic stainless steels is an associated increase in electrical resistance over time, due to the oxide growth. Further, the migration of chromium via chromia-scale evaporation into solid oxide fuel cell (SOFC) cathodes can result in degradation in cell electrochemical performance. In this research, manganese and cobalt were deposited by the pack cementation method onto Crofer 22 APU ferritic stainless steel. Isothermal and cyclic oxidation was carried out to evaluate the role of coating materials during oxidation. Area-specific resistance (ASR) of the Mn-Co-coated substrates was also tested at 800°C. The results demonstrate that the coating layer transforms to MnCo 2 O 4 , CoFe 2 O 4 , CoCr 2 O 4 , and Co 3 O 4 spinels during oxidation. This scale is protective, and acts as an effective barrier against chromium migration into the outer oxide. Mn-Co oxide and cobalt oxides also cause a reduction in ASR, in comparison to that of bare steel.

show abstract

“…The setup was similar to that described in the previous study [23]. Platinum wires were spot welded to one side of two identical polished samples to provide electrical connections.…”

Section: Methodsmentioning

confidence: 99%

Oxidation and Electrical Behavior of a Ferritic Stainless Steel with a Mn–Co-Based Coating for SOFC Interconnect Applications

Ebrahimifar

Zandrahimi

2015

Oxid Met

Self Cite

View full text Add to dashboard Cite

Protective coatings with high electrical conductivity that resist oxide scale growth are required for stainless steel interconnect materials in the long-term durable operation of solid oxide fuel cells. This work evaluates the oxidation and electrical behavior of Crofer 22 APU ferritic stainless steel coated with manganese and cobalt by electrodeposition. Isothermal and cyclic oxidation (800°C in air) tests were done to evaluate the role of the coating layer during oxidation. Area-specific resistance (ASR) of the coated and uncoated substrates was also tested at 800°C in air. Results show that the coating layer transforms into Mn 1.5 Co 1.5 O 4 spinel during oxidation. The mass gain and spallation indicated that the formation of Mn-Co spinel improves the high temperature oxidation. These spinels also cause a reduction in ASR for electroplated substrates (12.42 mX cm 2 ) as compared to uncoated ones (38.74 mX cm 2 ) after 400 h of isothermal oxidation at 800°C.

show abstract

Oxidation and electrical behavior of AISI 430 coated with cobalt spinels for SOFC interconnect applications

Cited by 51 publications

References 47 publications

Highly Dense Mn-Co Spinel Coating for Protection of Metallic Interconnect of Solid Oxide Fuel Cells

Highly Dense Mn-Co Spinel Coating for Protection of Metallic Interconnect of Solid Oxide Fuel Cells

Oxidation and Electrical Behavior of Mn-Co-Coated Crofer 22 APU Steel Produced by a Pack Cementation Method for SOFC Interconnect Applications

Oxidation and Electrical Behavior of a Ferritic Stainless Steel with a Mn–Co-Based Coating for SOFC Interconnect Applications

Contact Info

Product

Resources

About