One-Pot Synthesis of Biocompatible Glycine Protected Chromium Doped ZnS Nanoparticles and their Optical Properties

Abstract

Here in, we report the synthesis and characterization of Chromium doped Zinc Sulfide nanoparticles (ZnS NPs). Initially, ZnS NPs are synthesized by bio-compatible glycine cap using simple one-pot co-precipitate method, and further it is doped by Chromium. The structure and morphology of these ZnS NPs was confirmed by X-Ray Diffractometry (XRD) and Scanning Electron Microscope with Elementary Dispersive Spectrum (SEM with EDS) techniques. The optical characterization techniques reveal that the Chromium doping affected the absorption and photoluminescence properties of the NPs. Photoluminescence of these NPs shifts from 384 nm to 428 nm upon Chromium doping. By using Tauc plot we obtained the energy band gap of 4.7 eV and it reduces to 3.9 eV for Chromium dope. The resultant ZnS NPs have size of 2.17nm and 1.86nm (with Chromium doping), also it gives Cubic Zinc blend phase as proved by XRD. The instrumentation techniques SEM with EDS, XRD, FTIR confirms that high purity Chromium doped ZnS NPs can be obtained by the proposed simple, low cost and highly effective method.

Compositing of MOFs with ceramic and nanoparticles for efficient and rapid adsorptive desalination of artificial seawater or NaCl solution

“…For ZnO nanoparticles, the bands manifested at 435 and 616 cm −1 are assigned to the typical stretching mode of the Zn–O bond. 28,29 The band that appeared at 3189 cm −1 is attributed to the MIL88A(Fe) and a similar band was reported by. 30 For α-cordierite ceramic, the signals appeared at 1169 and 859 cm −1 attributed to AlO 4 and SiO bonds.…”

Catalytic Hydrogen Evolution from H2S Cracking over CrxZnS Catalyst in a Cylindrical Single-Layered Dielectric Barrier Discharge Plasma Reactor

“…The peak at 3700 cm −1 was due to O―H stretching vibration. This peak shows an alcohol group of compounds with intermolecular forces based on their structure [ 19 ]. The peaks at 1588 cm −1 and 1020 cm −1 exhibited the same amines groups with no intermolecular force at medium peaks.…”