Natural and Synthetic Fibers for Hybrid Composites

In engineering applications, natural fiber composites must comply with fire requirements including the use of flame retardant. Furthermore, biocomposites are known to be water sensitive. Whether flame retardants affect the water sensitivity and whether water absorption affects the fire behavior and the mechanical performance of biocomposites are the two main topics addressed in this work. In this study, a flax fiber/epoxy composite flame retardant with 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) or aluminum diethyl phosphinate (AlPi) was aged in humid atmosphere or by immersion in water. Water absorption kinetics revealed that DOPO induces an increase in equilibrium water content by approximately a factor of 2 due to its intrinsic hygroscopicity and/or its plasticizing effect on the epoxy matrix. In contrast, AlPi does not significantly change the water sensitivity of the biocomposite. Mechanical testing highlighted that, whatever the FR, the evolution of mechanical properties with ageing is governed by the moisture content. The drop of elastic modulus was attributed to a decrease in fiber rigidity due to plasticization, while the increase in tensile strength was assigned to an increase in fiber/matrix friction due to fiber swelling. As regards flame retardancy, only the highest water contents modified the fire behavior. For the AlPi containing biocomposite, the water release resulted in an increase by 50% of the time to ignition, while for the DOPO flame retardant biocomposite the water release was mainly postponed after ignition.

Section: Introductionmentioning

confidence: 99%

Effect of Hygrothermal Ageing on the Mechanical and Fire Properties of a Flame Retardant Flax Fiber/Epoxy Composite

Campana¹,

Léger²,

Sonnier³

et al. 2022

“…[ 7 ]. On the other hand, natural fiber reinforced polymer composites exhibit quite remarkable mechanical properties but far lower than synthetic counterparts [ 8 , 9 , 10 ]. To optimize parameters such as strength, cost, etc., and minimize the hazardous environmental effects, hybridization of natural and synthetic fiber has been performed.…”

Section: Introductionmentioning

confidence: 99%

Comparative Analysis of Erosive Wear Behaviour of Epoxy, Polyester and Vinyl Esters Based Thermosetting Polymer Composites for Human Prosthetic Applications Using Taguchi Design

Khare¹,

Dahiya²,

Gangil

et al. 2021

Self Cite

In polymer composites, synthetic fibers are primarily used as a chief reinforcing material, with a wide range of applications, and are therefore essential to study. In the present work, we carried out the erosive wear of natural and synthetic fiber-based polymer composites. Glass fiber with jute and Grewia optiva fiber was reinforced in three different polymer resins: epoxy, vinyl ester and polyester. The hand lay-up method was used for the fabrication of composites. L16 orthogonal array of Taguchi method used to identify the most significant parameters (impact velocity, fiber content, and impingement angle) in the analysis of erosive wear. ANOVA analysis revealed that the most influential parameter was in the erosive wear analysis was impact velocity followed by fiber content and impingement angle. It was also observed that polyester-based composites exhibited the highest erosive wear followed by vinyl ester-based composites, and epoxy-based composites showed the lowest erosive wear. From the present study, it may be attributed that the low hardness of the polyester resulting in low resistance against the impact of erodent particles. The SEM analysis furthermore illustrates the mechanism took place during the wear examination of all three types of composites at highest fiber loading. A thorough assessment uncovers brittle fractures in certain regions, implying that a marginal amount of impact forces was also acting on the fabricated samples. The developed fiber-reinforced polymer sandwich composite materials possess excellent biocompatibility, desirable promising properties for prosthetic, orthopaedic, and bone-fracture implant uses.

“…In recent years, the development of sustainable and eco-friendly high-performance materials has been addressed thanks to a growing ecological responsiveness. Hybrid composite materials constituted by polymeric matrices reinforced with both natural and synthetic fibers represent a potentially effective option [ 1 , 2 ]. Tailoring an adequate design of the constituents, a cost-effective, sustainable hybrid composite laminate applicable in structural contexts, could be acquired.…”

Section: Introductionmentioning

confidence: 99%

Effect of Glass Fiber Hybridization on the Durability in Salt-Fog Environment of Pinned Flax Composites

Fiore

Calabrese

2021

The aim of the present paper is to evaluate the effect of the hybridization with external layers of glass fibers on the durability of flax fiber reinforced composites in severe aging conditions. To this scope, full glass, full flax and hybrid glass–flax pinned laminates were exposed to a salt-fog environment for up to 60 days. Double-lap pinned joint tests were performed to assess the pin-hole joints performances at varying the laminate stacking sequence. In order to better discriminate the relationship between the mechanical behavior and the fracture mechanisms of joints at increasing the aging time, different geometries (i.e., by varying both the hole diameter D and the free edge distance from the center of the hole E) were investigated after 0 (i.e., unaged samples), 30 and 60 days of salt-fog exposition. It was shown that the hybridization positively affects the mechanical performance as well as the stability of pinned composites: i.e., improvements in both strength and durability against the salt-fog environment were evidenced. Indeed, the hybrid laminate exhibited a reduction in the bearing strength of about 20% after 60 days of aging, despite to full flax laminate, for which a total reduction in the bearing strength of 29% was observed. Finally, a simplified joint failure map was assessed, which clusters the main failure mechanisms observed for pinned composites at varying aging conditions, thus assisting the joining design of flax–glass hybrid laminates.