Multiscale frictional behaviors of sp2 nanocrystallited carbon films with different ion irradiation densities

Abstract

sp2 nanocrystallited carbon films with large nanocrystallite sizes, smooth surfaces, and relative high hardness were prepared with different ion irradiation densities regulated with the substrate magnetic coil current in an electron cyclotron resonance plasma sputtering system. Their multiscale frictional behaviors were investigated with macro pin-on-disk tribo-tests and micro nanoscratch tests. The results revealed that, at an ion irradiation density of 16 mA/cm2, sp2 nanocrystallited carbon film exhibits the lowest friction coefficient and good wear resistant properties at both the macroscale and microscale. The film sliding against a Si3N4 ball under a contact pressure of 0.57 GPa exhibited a low friction coefficient of 0.09 and a long wear life at the macroscale. Furthermore, the film sliding against a diamond tip under a contact pressure of 4.9 GPa exhibited a stable low friction coefficient of 0.08 with a shallow scratch depth at the microscale. It is suggested that sp2 nanocrystallites affect the frictional behaviors in the cases described differently. At the macroscale, the contact interface via the small real contact area and the sp2 nanocrystallited transfer layer dominated the frictional behavior, while the sp2 nanocrystallited structure in the film with low shear strength and high plastic resistivity, as well as the smooth surface morphology, decided the steady low nanoscratch properties at the microscale. These findings expand multiscale tribological applications of sp2 nanocrystallited carbon films.

A review of advances in tribology in 2020–2021

“…Apart from that, other carbon-based materials also exhibited superior tribological properties, such as fullerene-like carbons [182], carbon fibers [183], and carbon-coating coatings [184]. Liu et al [182] found that the lower hydrogen concentration in the preparation process of fullerene-like carbons was beneficial to enter the low friction state.…”

A review on diamond-like carbon-based films for space tribology

“…Upon increasing the dose, agitated He bubbles on the film surface easily burst, and then holes formed, which led to lower mechanical properties and poor wear properties. However, Hu et al [103] found that nanocrystallited sp 2 C showed a lower COF and extended service life after ion radiation.…”

Ion energy-induced nanoclustering structure in a-C:H film for achieving robust superlubricity in vacuum

“…In addition, the bonding state of carbon skeleton is also important for the realization of superlubricity. Both experimental and simulation results suggest that the tribo-induced rehybridization of carbon network from sp 3 to sp 2 and their reorientation towards layerlike structure may also account for the formation of easy-shearing interfaces, which contributes to the selflubricating behavior [47][48][49][50][51][52][53][54][55][56][57][58][59]. However, for traditional a-C:H synthesized with hydrogen and alkanes, the sp 2 ratio decreases with hydrogen content [60], which makes it hard to investigate the influences of bonding hybridization and surface passivation independently.…”