In this study, the bioactivity and the mechanical properties (Mechanical compressive stresses, Hardness, and density) of bioglass (BG) and bioglass/graphene oxide (BG/GO) were investigated. Bioglass in chemical composition [60SiO2_35CaO_5P2O5] was prepared via the sol-gel method. GO was added to the bioglass (BG) with different contents (0.5, 1, 2, and 3) wt.% named as 0.5%GO, 1%GO, 2%GO, and 3%GO samples respectively. The synthesized specimens were characterized by several techniques (FT-IR, XRD, and SEM). Compressive stresses, Hardness, and density were studied also by different techniques to obtain the optimum Mechanical samples. The biological activity was studied by an in-vitro test in simulated body fluid (SBF) for 33 days. Results showed that: the 0.5%GO sample exhibited optimum mechanical compressive strength by approximately 82% compared to the BG sample. Hardness was increased from 0.5%GO sample up to 1%GO sample compared to BG sample and gradually decreased in 2%GO Sample and 3%GO. Bioactivity results showed deposition of HA layer on the bioglass surface and there was no significant change in it with the addition of graphene oxide.