Linear Copolymer of N-Isopropylacrylamide and 2-Hydroxyethylacrylate: Synthesis, Characterization and Monomer Reactivity Ratios

Abstract

Ñopolymerization of N-isopropylacrylamide (NIPAAm) with 2-hydroxyethyl acrylate (2-HEA) carried out by solvent ethanol solution method, at 60 0 C, using Azoisobutyronitrile (AIBN) as an initiator. The hydrophilic copolymers were characterized by elemental analysis, DSC, TGA and turbidimetric method. The results showed thermal stability increase with increase of NIPAAm in the copolymers. It was found that copolymer solutions have lower critical solution temperature (by turbidimetric analysis). The reactivity ratios of monomers were determined using linear methods like Fineman-Ross and Kelen-Tudos. The reactivity ratios of r 1 and r 2 were found to be 0,

Hydrogels based on N‐isopropylacrylamide and 2‐hydroxyethylacrylate: synthesis, characterization and investigation of their antibacterial activity

“…In the linear copolymer of NIPAAm with 2‐HEA, when the NIPAAm content in the initial monomer mixture is 70 mol, the phase transition temperature varies between 30 and 35 °C. This area is considered to be a phase transition zone of PNIPAAm 15 . It is known that the range of normal body temperature is 36–37 °C.…”

“…This area is considered to be a phase transition zone of PNIPAAm. 15 It is known that the range of normal body temperature is 36-37°C. The volume phase transition temperature of hydrogel M2 is 35-40°C.…”

“…This was mainly due to the higher reactivity of the NIPAAm ratio than the 2-HEA ratio. [14][15][16] In this study, P(NIPAAm-co-2-HEA) hydrogels were synthesized by free-radical copolymerization. These hydrogels were characterized by TGA, DSC and SEM.…”

“…It has been shown that increase in the ratio of NIPAAm in the copolymer from 70% to 90% led to growth in the molecular weight. This was mainly due to the higher reactivity of the NIPAAm ratio than the 2‐HEA ratio 14–16 …”

Swelling kinetics of poly(2HEA-AA) hydrogels in different solutions

“…Осы полимерлерге деген сұраныстың көп болуы көптеген зерттеушілердің қызығушылығын тудырды. Танымал полимерлердің қолданыс аясы полимердің бағалы қасиеттерімен байланысты екені және осы қасиеттерін белгілі параметірлермен реттеп, тиімді пайдалануға болатынын көптеген зерттеушілердің зерттеу жұмыстарында қарастырылды және жақсы нәтижелерге қол жеткізілді [1][2][3][4][5] Гидрогельдерді өздерінің құрамында сұйықтықтың көп мөлшерін ұстап тұра алатын (сіңіріп алатынын) композициялық материалдардың ерекше класына жатқызуға болатынын жоғарыда қарастырғамыз. Осы гельдің сұйықтарды сіңіру қабілеті өндірісте ағын сулардың құрамындағы әртүрлі металл иондарынан және бояғыш заттардан тазарту үшін, ал медицинада жарадағы іріңді заттарды сіміріп шығарып тастауда, дәрілік заттарды қажетті орынға тасымалдауда т.б көптеген салаларда осы гидрогельдердің ісіну жиырылу механизімін пайдаланады.…”