“…For the electrospinning, a solution containing 15 wt % of ammonium tetrathiomolybdate ((NH 4 ) 2 MoS 4 , ATTM, Alfa Aesar, Ward Hill, MA, USA) and 15 wt % of poly(styreneacrylonitrile, SAN, Mw = 1,300,000) dissolved in 10 mL of N,N-dimethylformamide (DMF, Sigma-Aldrich, Burlington, MA, USA), was prepared on the hot plate by stirring the solution at 70 • C for 12 h. The solution was electrospun by applying a high voltage of 15 kV using an electrospinning machine (NanoNC, Seoul, South Korea). After the electrospinning, the electrospun NFs were thermally treated under H 2 /Ar (4/96, v/v) surroundings at 450 • C for 2 h and under a pure Ar (99.999%) atmosphere at 800 • C for 6 h, respectively [17,22]. These processes were performed to make the MoS 2 @CNFs.…”