Joints realized by sintering of pressureless Ag paste

Abstract

Purpose The purpose of this paper was to investigate an influence of a low temperature pressureless sintering process of silver paste on the quality of sintered joints. Design/methodology/approach The authors analyzed various curing conditions of the paste during its sintering process: 175°C/90 min, 200°C/60 min, 250°C/30 min, 250°C/60 min, 350°C/30 min and 350°C/60 min. They analyzed an influence of the surface plating applied on a ceramic substrate/layer (Cu, Ag, AgPt and Au thick film) on the joints quality. The authors analyzed microstructure and electrical resistance of the joints. They evaluated these properties from the point of view of thermal aging process and changing resistance, after a constant current loading of the sintered joints. Findings The nanoscale pressureless silver paste can be applied for replacing a pressure-assisted micro-sized silver paste. It was found that the quality of the metal plating applied on the ceramic substrate/layer has a significant impact on the quality of the sintered joints. Copper and AgPt plating have better impact on quality of sintered joints in compare with Ag plating. Originality/value This investigation of the quality of the pressureless sintered joints at the silver-silver interface reveals an evident cracking immediately after the silver paste curing. Rapid sintering process typical for silver-based films on the substrate is because of the inter-diffusion between the micro and nanoparticles of silver at interfacial interface.