Isothermal Fatigue of 63Sn-37Pb Solder

Abstract

The effects of aging, strain range, hold time at maximum strain and temperature on the isothermal fatigue life of bulk 63Sn-37Pn solder samples over the total strain range (Δ εT) from 0.3 to 3.0 percent (tension-tension) and within the temperature range of 25° C to 100° C were studied. The cycles to failure (Nf) were defined as the number of cycles at which the ratio of the maximum tensile stress to the maximum compressive stress starts to drop appreciably. Fatigue life increases rapidly after a day or two of aging after heat treatment at 150° C for 2 hours followed by air cooling but levels off after a week. The log of fatigue life decreases linearly with increasing log of plastic strain range above Δ εT = 0.6 percent. Hold time at maximum strain dramatically decreases the cycles to failure, however, an increase of hold time more than a few minutes eventually leads to a constant Nf. Temperature variation from 25°C to 100° C was found to have little effect on the fatigue life of the solder in tests with and without hold time. Separation of Pb-rich and Sn-rich phases and cracking of the Sn-rich phases are the main modes of fracture under all conditions used. Damage is concentrated along crisscrossing shear bands oriented approximately 45 deg to the load direction.

Microstructural changes in eutectic tin–lead alloy due to severe bending

“…Figure 3 of Ref. [6] schematically illustrates this distribution function. This quasi-equilibrium approximation is similar to the Saha equation describing quasi-equilibrium in plasma physics [9].…”

“…In the fwst approximation, the carriers in the current filaments can be described by a distribution function which approaches a quasi-equilibrium Maxwell-BoItzmann distribution function, characterized by a carrier temperature which is much larger than the lattice temperature [4,6,8]. Figure 3 of Ref.…”

“…The Hjalmarson et al theory [4,6] explains the main characteristics of lock-on. It is based on the collective impact ionization of charge carriers by optically injected carriers.…”

“…It is based on the collective impact ionization of charge carriers by optically injected carriers. This leads to a stable, filamentary current, sustained by a reduced field [4] and to a bistable, S-1ike current-voltage characteristic for the switch [6].…”

“…In the present paper, ive present preliminmy results, obtained using the collective impact ionization theory of Hjalmarson et al [4,6], of a study of some of the steady state properties of these lock-on current fiIaments.…”