Initiation and Propagation Processes of Internal Fatigue Cracks in β Titanium Alloy Based on Fractographic Analysis

Abstract

Uniaxial fatigue tests were conducted for a β titanium alloy Ti-22V-4Al up to a very high cycle fatigue (VHCF) regime. The initiation and propagation processes of the internal fatigue cracks were investigated using 3D fractographic analysis. Multiple facets were observed at the crack initiation site. Three facet initiation models were proposed based on the surface appearances and the 3D facet bonding patterns of the multiple facets, and the major facet was determined to be the true crack initiation site. Using the size of the major facet, a Tanaka–Akiniwa model, which can determine the material constants for the Paris law using only conventional fatigue tests, was applied to reveal the propagation process of the internal cracks. A reverse fatigue life prediction was also conducted to evaluate the accuracy of the material constants obtained using the Tanaka–Akiniwa model. When the facet initiation models were applied, the predictions showed less deviation and better agreement than when the facet initiation process was not considered. The findings of this study indicate that the formation of multiple facets in β titanium alloys is sequential rather than simultaneous.

Effect of HIP post-processing at 850 °C/200 MPa in the fatigue behavior of Ti-6Al-4V alloy fabricated by Selective Laser Melting

“…The mechanism of fatigue crack initiation in the SLM α + β titanium alloys is well known and reported in detail by many authors [49][50][51][52][53] and is related to the facet formation in alpha phase. The crack initiation…”