Influência da cal hidratada nas idades iniciais da hidratação do cimento Portland - estudo em pasta.

Abstract

In the last decades, scientific and technological progress has shown a significant advance in the process of obtaining lime; however, there is gap knowledge with relation to its action when employed together with Portland cement. The use of lime in finishing mix mortars has only been positively associated to the fresh state plasticity and ability to deformation in the hardened state. It is necessary to collect data about the role of lime in the gradual development of the properties of mortars in the fresh state, linked to cement hydration. Such knowledge is important to develop formulas which can meet the required performance in different uses. The current demand of sustainable materials has favored the addition of minerals to the composition of Portland cement, and hydrated lime as an extern source of calcium, is a feasible alternative to the composition of byproducts and mixtures to be used as alternative binders. This research focused the cement-lime interaction aiming at identifying relevant chemical and physical phenomena which succeed the addition of water to the system. The paste study characterized the early ages of hydration by means of isothermal calorimetric, thermogravimetric, X-ray diffraction in material in the fluid state analysis collecting data in a consecutive basis. The experiments were carried out by using two proportions of Portland cement type CP II E with hydrated lime types CH I and CH III, calcic and dolomitc, respectively. By adding lime CH I to the cement-water system, calcium hydroxide is abundantly incorporated, with immediate saturation by means of hydroxide ions and calcium ions. The addition of lime CH III, also incorporates, in greater amount, finely ground limestone. Due to chemical effect because of the presence of lime, there is alteration in speed of hydration, forming products characteristics to the cement hydration process. Due to physical effect, the filler and the lime insoluble fraction of calcium hydroxide, present in the saturated environment, work as facilitators to the precipitation of the hydrated phases. The combined effect of these two phenomena accelerated hydration of Portland cement, mainly in the induction period, when ettringite and hydrated calcium aluminates formation reactions prevail. The advancement made in terms of knowledge permits to broaden comprehension on the behavior of mixtures in early stages, when hardening and consolidation processes are applied to mortars and help rheologic studies which involve their application. The understanding of the hydration mechanism in the presence of lime sets a base to study additions of active minerals to the clinker and produce new sustainable cementious compounds.

Atividade pozolânica de adições minerais para cimento Portland (Parte I): Índice de atividade pozolânica (IAP) com cal, difração de raios-X (DRX), termogravimetria (TG/DTG) e Chapelle modificado

“…A área específica BET das adições ativas é significativamente superior à área das adições inertes, o que não se verifica por análise da área específica Blaine. Quarcioni [15], ao obter a área específica para o cimento CP II E de 0,39 m 2 /g pelo método Blaine e 1,10 m 2 /g pelo método BET, indica que a área específica Blaine é obtida a partir de um fluxo contínuo de ar, limitando-se à superfície externa das partículas, enquanto o método BET mede também a superfície interna dos poros abertos e interconectados. Portanto, a área específica BET é mais fidedigna para se inferir a disponibilidade de área das partículas para a interação com as espécies químicas presentes no meio aquoso.…”

Avaliação do efeito mitigador do pó de concreto proveniente de RCD no ataque por sulfatos de sódio em barras de argamassa

“…Os resultados demonstram que quanto maior a substituição, maior a expansão resultante, além de todos percentuais levarem a um aumento na expansão em relação a referência, evidenciando que a adição por pó de concreto não possui potencial em mitigar o ataque por íons sulfatos de origem externa. As imagens obtidas das microestruturas das argamassas estão de acordo com o apresentado pela literatura tanto na morfologia dos cristais identificados [2,17], quanto no comportamento frente ao ataque por íons sulfato [4,18]. A Figura 5 apresenta a microestrutura da argamassa de referência e da argamassa contendo 20% de pó de concreto, após 100 dias de imersão em solução saturada de cal.…”

Estudo da reologia de pastas cimentícias contendo resíduo de tijolo cerâmico moído e metacaulim

“…QUARCIONI [18] mostrou que o estudo em pastas cimentícias é de grande valia quando se quer avaliar o comportamento do material durante seu manuseio e aplicação.…”