Influence of Post Weld Heat Treatment on the Grain Size, and Mechanical Properties of the Alloy-800H Rotary Friction Weld Joints

Abstract

This study evaluated the microstructure, grain size, and mechanical properties of the alloy 800H rotary friction welds in as-welded and post-weld heat-treated conditions. The standards for the alloy 800H not only specify the composition and mechanical properties but also the minimum grain sizes. This is because these alloys are mostly used in creep resisting applications. The dynamic recrystallization of the highly strained and plasticized material during friction welding resulted in the fine grain structure (20 ± 2 µm) in the weld zone. However, a small increase in grain size was observed in the heat-affected zone of the weldment with a slight decrease in hardness compared to the base metal. Post-weld solution heat treatment (PWHT) of the friction weld joints increased the grain size (42 ± 4 µm) in the weld zone. Both as-welded and post-weld solution heat-treated friction weld joints failed in the heat-affected zone during the room temperature tensile testing and showed a lower yield strength and ultimate tensile strength than the base metal. A fracture analysis of the failed tensile samples revealed ductile fracture features. However, in high-temperature tensile testing, post-weld solution heat-treated joints exhibited superior elongation and strength compared to the as-welded joints due to the increase in the grain size of the weld metal. It was demonstrated in this study that the minimum grain size requirement of the alloy 800H friction weld joints could be successfully met by PWHT with improved strength and elongation, especially at high temperatures.

The Influence of Arc Welding Process on the Mechanical and Microstructural Characteristics of Low Carbon Steel in a Corrosive Environment

“…These orientations largely show noticeable differences in the microstructures as seen from the average grain size measurements of BM, Corse Grain (CGHAZ), Fine Grain (FGHAZ), Intera-critical (ICHAZ), and Weld zone (WZ) as 5, 14 , 9 , 2 , and 23 μm, respectively. It is a consequential increase of average grain size from HAZ to the Weld zone [22,23] as shown in excellent toughness properties. [24,25,26] When the concentration of Mn is low, Cr has a better influence on the weld structure.…”

Enhancing the Weld Quality of Polylactic Acid Biomedical Materials Using Rotary Friction Welding

“…Eliseev et al [7] explored the microstructural changes occurring in the transfer layer of aluminum (Al) alloy welding parts, uncovering a decrease in grain size and volume fraction toward the center of the layer. Anwar et al [8] investigated the microstructure of alloy 800H of welding part using RFW after heat treatment, successfully achieving the minimum grain size. Khalaf et al [9] investigated the heat generation of different tool components.…”

Mechanical Performance and Microstructural Evolution of Rotary Friction Welding of Acrylonitrile Butadiene Styrene and Polycarbonate Rods

“…Optimization of the duration of the friction phase of the friction-welding process was also investigated. Anwar et al [15] investigated the microstructure, mechanical properties, and grain size of the alloy after RFW. The minimum grain size was successfully met by postweld heat treatment with improved elongation and strength.…”