Influence of Laser Treatment on the Creep of the Ti-6Al-4V Alloy

Abstract

Titanium and its alloys are excellent materials for structural applications in components submitted to high temperatures because of their high strength, weight ratio, good corrosion resistance, and microstructural stability. However, the affinity to oxygen is one of the main factors that limit their application as structural materials at high temperatures. The objective of this work was to estimate the influence of laser treatment on the creep of a Ti-6Al-4V alloy. Constant load creep tests were conducted at 873 K (600°C) in a standard creep machine at a stress of 125 to 319 MPa. Samples with a gage length of 18.5 mm and a diameter of 3.0 mm were used for all tests. It was observed that the effect of the oxidation was smaller and the behavior of the creep curves showed that the life time in laser treated samples was better than in the received samples. An increase of ductility of final strain and in the lifetime for the lasertreated material was observed. The decrease of the steady-state creep occurred in conjunction with the oxidation process reduction, showing that for the Ti-6Al-4V alloy, the lifetime is affected strongly by the laser treatment with an increase in this superficial protection.

Avaliação dos parâmetros de nitretação por laser de CO2 no aço maraging 18Ni (300) para melhoria da resistência à oxidação

“…pelo governo brasileiro, a utilização do aço maraging no passado não era possível, sendo necessárias outras soluções para a sua substituição como, por exemplo, o aço 300M que foi desenvolvido no Brasil para este propósito. Ainda que suas características mecânicas atendessem os requisitos para aplicação na indústria aeroespacial, estes aços não possuíam todas as vantagens do Maraging 300 por serem mais caros e de difícil processabilidade [2,3]. Com novas políticas de importações que viabilizaram a utilização do Maraging 300 em território nacional, o seu estudo se tornou de grande interesse para órgãos governamentais e empresas do ramo espacial, sendo assim, os estudos envolvendo este material que apresenta uma alta resistência mecânica sem perder sua maleabilidade, vêm sendo amplamente difundidos [4].…”

Heat Treatments Effects on Nickel-Based Superalloy Inconel 713C

“…The highest hardness had the eutectic carbides. So, more carbides, the macrohardness increases [10][11][12][13][14][15][16][17][18][19][20][21][22][23].…”

Análise do comportamento mecânico de ligas metálicas submetidas ao processo superplástico em matriz multidomo.

“…A durabilidade do material é bastante reduzida em meios corrosivos e atmosferas com gases quentes (REIS et al, 2004 Entretanto é importante ressaltar que mesmo com proteção a peça não está livre completamente de oxidação e após o processo uma fina camada pode ficar depositada sobre a superfície, empresas fabricantes de aeronaves como a Boeing utilizam usinagem química para remover a camada oxidada (ZHANG, 2014).…”