Inertización de lodos galvánicos para su incorporación a productos cerámicos

Abstract

Sludges produced by the physico-chemical treatments of waste waters generated by electroplating plants were physically and chemically characterised and incorporated in ceramic pastes. The influence of the amount of sludges added to a typical brick composition on the various processing steps and on the green and fired properties was studied. The environmental risks of the incorporation of these sludges rich in heavy metals such as Cr, Pb, Zn, Cu, Ni, etc. were evaluated by performing leaching tests on the fired products. The results showed that sludge contents up to 15 % could be incorporated without affecting significantly the physical characteristics of the ceramic products. Furthermore, a successful inertization of the pollutants was achieved.Key words: Recycling, Sludges, Heavy metals, Environment, Wastes. Inertizaci-n de lodos galv ‡nicos para su incorporaci-n a productos cer ‡micosSe han caracterizado desde el punto de vista qu'mico y f'sico lodos procedentes de las aguas residuales de procesos de galvanizado. Posteriormente se han incorporado a pastas cer ‡micas, convencionales de la industria ladrillera, estudi ‡ndose la influencia de las cantidades a-adidas sobre las propiedades de los materiales tanto en verde como en el producto final y durante las distintas etapas de fabricaci-n. Se evaluaron los riesgos medioambientales derivados de la incorporaci-n de los metales pesados, tales como Cr, Pb, Zn, Cu, Ni etc, presentes en los lodos, mediante la realizaci-n de ensayos de lixiviado. Los resultados indican que puede incorporarse hasta un 15% en peso de dichos lodos, sin que se produzcan cambios significativos en las propiedades f'sicas de los materiales cer ‡micos obtenidos. Se ha obtenido, asimismo, un procedimiento viable de inertizaci-n de los agentes contaminantes.

Pigments from spent Zn, Ni, Cu, and Cd electrolytes from electroplating industry

“…There are not many studies that describe production of commercial goods (Carneiro et al 2018). Articles (Costa et al 2008;Ferreira et al 1999;Abdurakhmanov et al 2000) present the results of using galvanic sludge in the production of ceramic products for various purposes such as clay bricks (Pérez-Villarejo et al 2015), cement clinker (Espinosa and Tenório 2000;Ract et al 2003), different glasses (Andreola et al 2006;Silva et al 2008), and obtaining pigments (Cheprasova and Zalyhina 2017;Andreola et al 2008).…”

Manufacture of Sustainable Clay Bricks Using Waste from Secondary Aluminum Recycling as Raw Material

“…It is therefore interesting to use different industrial waste in the manufacture of different construction materials, such as ceramic clay bricks. The ceramic industry presents enormous potential for the reuse and recovery of industrial waste [1,2,3,4,5,6,7]. The Spanish structural ceramic sector is the largest European producer, with about 30 million tons in 2007.…”

Efeito da adição de rejeito na redução de coração negro em cerâmicas vermelhas

“…Assim, diversos trabalhos foram publicados com o objetivo de introduzir diferentes rejeitos durante a produção de tijolos comerciais. A quantidade adicionada varia com o tipo de rejeito, com o objetivo de manter as propriedades dos tijolos em níveis aceitáveis, de modo a atingir aos requisitos das especificações [4][5][6][7].…”

“…Dentro da área siderúrgica foi relatada a adição, à massa cerâmica, de finos de areia de fundição, escórias de siderurgia em geral (com adição isolada ou em conjunto com precipitados de estação de tratamento de águas de curtume), escórias de alto forno, lamas de rejeito de indústrias de eletrodeposição de metais. [5][6][7][8][9][10]. Ligados ao setor energético, foram reportadas adições de resíduos de estação de tratamento de efluentes de campos petrolíferos e cinzas de combustão de carvão [4,11,12].…”