In vitro Evaluation of Tribocorrosion Induced Failure Mechanisms at the Cell‐Metal Interface for the Hip Implant Application

Abstract

In a hip joint environment, the bone-metal implant interface of an implant is exposed to the combined effect of wear and corrosion (tribocorrosion). This may create mechanical instability and cause early failure of the implants. The aim of this work was to investigate the tribocorrosion behavior of Ti6Al4V alloys in the presence of bone-forming cells cultured on its surface (cell-metal interface), using an electrochemical and tribological approach. The results showed that at a cathodic potential (À0.9 V), the presence of osteoblast-like cells and serum proteins in the media might induce a higher passivation rate of the oxide film, enhancing the corrosion resistance. However, when the surface is in steady state (0.7 V) they show a lower resistant to corrosion, increasing the susceptibility to corrosion.

Falhas em implantes de quadril

“…A tentativa da utilização de fibra de carbono não foi bem sucedida. Estudos de corrosão in vitro são um caminho para o aprimoramento desses materiais (Runa et al, 2017) Outro ponto importante a ser estudado, é o processo de fadiga, que é responsável por diversas falhas em implantes de quadril. O desenvolvimento de ligas com maior resistência à fadiga é necessário, assim como, cuidados no acabamento superficial dos implantes, que podem vir a resultar em concentradores de tensão, diminuindo drasticamente a vida do componente.…”