Improved Cellular Infiltration in Electrospun Fiber via Engineered Porosity

Abstract

Small pore sizes inherent to electrospun matrices can hinder efficient cellular ingrowth. To facilitate infiltration while retaining its extracellular matrix-like character, electrospinning was combined with salt leaching to produce a scaffold having deliberate, engineered delaminations. We made elegant use of a specific randomizing component of the electrospinning process, the Taylor Cone and the falling fiber beneath it, to produce a uniform, well-spread distribution of salt particles. After 3 weeks of culture, up to 4 mm of cellular infiltration was observed, along with cellular coverage of up to 70% within the delaminations. To our knowledge, this represents the first observation of extensive cellular infiltration of electrospun matrices. Infiltration appears to be driven primarily by localized proliferation rather than coordinated cellular locomotion. Cells also moved from the salt-generated porosity into the surrounding electrospun fiber matrix. Given that the details of salt deposition (amount, size, and number density) are far from optimized, the result provides a convincing illustration of the ability of mammalian cells to interact with appropriately tailored electrospun matrices. These layered structures can be precisely fabricated by varying the deposition interval and particle size conceivably to produce in vivo-like gradients in porosity such that the resulting scaffolds better resemble the desired final structure.

Polymeric Nanofibers in Tissue Engineering

“…These include salt leaching techniques, where salt crystals are mixed with the fibers during fabrication and leached after spinning. 62 Similarly, researchers have induced the formation of ice crystals on the collecting plate, which leads to larger pores in the construct after melting the ice crystals. 63 A dual electrospinning setup has been created with the additional stream of polymer serving to create a sacrificial fiber that is eluted after spinning, increasing the void space in the construct.…”

“…64 Although these strategies have successfully increased scaffold pore size, the mechanical strength of the constructs was reduced. 62 Recently, it was…”

Airbrushed Composite Polymer Zr-ACP Nanofiber Scaffolds with Improved Cell Penetration for Bone Tissue Regeneration

“…13 Synthesizing scaffolds where cells penetrate within networks and interact in both horizontal and vertical directions is still challenging and underreported. [14][15][16] Ideally, to better facilitate cell connectivity in all directions, fibrous scaffolds should have an open structure while providing biomimicking tissue morphology on both a micro and submicron scale. Adequate cell-material compatibility can potentially guide and promote cell growth, cell-cell communication, and order within a 3D matrix.…”

Engineering on the Straight and Narrow: The Mechanics of Nanofibrous Assemblies for Fiber-Reinforced Tissue Regeneration

“…116 Alternatively, pores may be introduced by including salt particles at the time of production and subsequently leaching the salt out. 121 In the former case, some increase in cell infiltration was observed, particularly when coupled with fluid flow through the scaffold thickness. In the latter case, salt crystals created planes of separation within the scaffold into which cells could migrate, though this compromised the overall structural integrity of the scaffold.…”