Effects of Passes on Equal Channel Angular Pressing of 6061 Aluminium Alloy

Banjongprasert, Chaiyasit; Domrong, C.; Chairuangsri, Torranin

doi:10.4028/www.scientific.net/amr.747.615

Cited by 3 publications

(1 citation statement)

References 5 publications

(4 reference statements)

Supporting

Mentioning

Contrasting

Order By: Relevance

“…ECAP has been applied to various engineering alloys especially aluminum alloys. Most of previous studies show that ECAP led to an improvement of mechanical and electrical properties of aluminum alloys [9,10]. However, there are arguments on the effects of severe plastic deformation on corrosion behaviours of aluminum alloys.…”

Section: Introductionmentioning

confidence: 99%

Characterization Of An Equal Channel Angular Pressed Al-Zn-In Alloy

Banjongprasert¹,

Jak-Ra²,

Domrong³

et al. 2015

Archives of Metallurgy and Materials

View full text Add to dashboard Cite

Equal channel angular pressing (ECAP) is a technique that creates a high accumulated strain in metals and results in ultrafine-grained structure. In this study, Al-5Zn-0.02In was processed by ECAP at a room temperature using route Bc through an ECAP die (press angle of Φ = 100• and Ψ = 20 • ). The samples were subjected to ECAP with 1, 2, 3 and 4 passes. The processed specimens were characterized using electron backscatter diffraction (EBSD). The results confirmed the grain refinement of the alloy after ECAP to an average grain size less than 5 µm after 4-pass ECAP. The microhardness test shows that the hardness increased with the number of passes. The hardness of the cross-sectional area of the sample was similar to that tested along the pressing direction.Keywords: Aluminum alloys, Equal channel angular pressing, Severe plastic deformation, Electron backscatter diffraction Metoda przeciskania w kanale kątowym (ang. Equal channel angular pressing; ECAP) prowadzi do powstania bardzo wysokich naprężeń, w wyniku czego otrzymuje się ziarna o bardzo drobnej strukturze. W niniejszej pracy, stop Al-5Zn-0,02In wytwarzano metodą ECAP w temperaturze pokojowej, wykorzystując ścieżkę Bc przez matrycę ECAP (kąty krzywizny: Φ = 100• i Ψ = 20 • ). Próbki poddano ECAP z 1, 2, 3 i 4 przejściami. Otrzymane próbki badano metodą dyfrakcji elektronów wstecznie rozproszonych (ang. electron back scatter diffraction; EBSD). W stopie otrzymanym metodą ECAP z 4 przejściami, średnia wielkość ziaren wynosiła mniej niż 5 µm. Badania mikrotwardości wykazały, że twardość zwiększała się wraz z liczbą przejść. Twardość zmierzona w poprzek próbki byłą porównywalna do tej mierzonej wzdłuż osi nacisku.