Dry Sliding Wear Studies on Sillimanite and B4C Reinforced Aluminium Hybrid Composites Fabricated by Vacuum Assisted Stir Casting Process

Abstract

This paper presents the results of studies to understand the influence of hybridisation on mechanical and tribological behaviour as well as dry sliding wear of aluminium metal matrix composites. Sillimanite and boron carbide (B4C) were used as primary and secondary reinforcements and pure aluminium was used as the matrix material. The composite was fabricated by using a vacuum assisted stir casting process. Different research instruments were used, including a scanning electron microscope with EDX spectrometer, a surface measurement device, a thermal image analyser, as well as a tribotester. The results show that tensile, impact strength and hardness of the hybridised composites are superior (a step ahead) than unreinforced and primary composites. The wear behaviour of the fabricated specimens was tested for the dry sliding wear behaviour under the load range of 10–50 N with the steps of 20 N for the sliding velocities 0.75, 1.5 and 2.25 m/s over a distance of 1000 m. The wear rate increased with load and decreased as the wt.% of reinforcement increased. The wear rate of the composite with 10 wt.% Al2SiO5 was approximately 44% lower than that of the composite with 5 wt.% Al2SiO5. The same dependence was noted for hybrid composite (5 wt.% Al2SiO5 + 5 wt.% B4C)—the wear rate was approximately 50.8% lower than that of the composite with 5 wt.% Al2SiO5 under the same test condition. The friction coefficient decreased as the weight percentage of the reinforcement (Al2SiO5 and B4C) increased due to the uniform distribution of the reinforcement on the surface of the composites. The main wear mechanism of the studied materials was abrasion wear. The wear mechanism of the composite had tribochemical type. It involved the oxidation and transfer of the material, which formed protective tribolayers ensuring an additional sliding process. The mechanism that played the main role in the wear process of the composites was a combination of abrasive, adhesive and oxidative wear.

Comparative Study on Mechanical Property and Fracture Behavior of Age-Hardened LM4 Monolithic Composites Reinforced with TiB2 and Si3N4

“…As the density of both these reinforcements is higher than that of the Al alloys, it is very difficult to fabricate composites with uniform reinforcement distribution. As per Pethuraj et al [7], the best method to fabricate AMMCs was the stir casting method, which provided better bonding between the matrix and reinforcement material and also provided better distribution of reinforcements. Bernoulli et al [8] used semisolid stirring and ultrasonic processing methods to overcome density-related issues by adding highly dense graphene powder to A319 alloy.…”

A Review on Abrasive Wear of Aluminum Composites: Mechanisms and Influencing Factors

“…There are various methods for producing aluminum composites, such as stir casting [4,5], powder metallurgy [6,7], centrifugal casting [8,9], ultrasonication-assisted stir casting [3,10], and spray casting [11,12]. Stir casting and powder metallurgy are the most common techniques and have been extensively researched due to their versatility, ease of use, and commercial feasibility.…”