In drop forging of parts for the transport industry the classical quench and tempering (QT) of alloyed steels is nowadays substituted by direct continuous cooling (CC) of microalloyed steels with elimination ofquench cracking and expensive straightening and stress relieving cycles. Nevertheless, there are some limitations on strength and toughness achievable by this technique. On two commercial medium carbon (0.3%C) steels microalloyed with vanadium or vanadium and titanium, modified forging parameters and a new two-step cooling (TSC) strategy combined with an additional annealing were applied. Some increase in manufacturing costs, when compared to CC, can be justified by a significant increase in strength and ductility. The improvements attainable through such a modified treatment give evidence of the large potential of multi-phase ferrite-containing microstructures as a substitute ofa tempered martensite. Neuartige Schmiedenachbehandlung von mikrolegierten Stahlen mit mittlerem Kohlenstoffgehalt. Beim Gesenkschmieden von Kraftfahrzeugteilen wird heutzutage die klassische VergOtung (QT) von legierten Stahlen durch eine direkte kontinuierliche AbkOhlung (CC) von mikrolegierten Stahlan ersetzt. Dadurch kennan die RiBbiidungsgefahr eliminiert und das SpannungsarmglOhen und das Richten eingespart werden. Mit dieserTechnologie lassen sich allerdings nicht immer zufriedenstellende Festigkeits-und Zahigkeitseigenschaften erreichen. Auf zwei handelsObliche mit Vanadium oder mit Vanadium und Titan mikrolegierte Stahle mit mittlerem Kohlenstoffgehalt (0,3% C) wurden modifizierte Umformparameter und eine neuartige zweistufige AbkOhlung (TSC) in Kombination mit einem nachtraqllchan GIOhen angewendet. Diese im Vergleich zurCCaUfwendigere Behandlung kann durch eine bemerkenswerte Verbesserung von Festigkeit und Duktilitat gerechtfertigt sein. Die erreichten Ergebnisse verdeutlichen das Potential von mehrphasigen ferrithaltigen GefOgen, die als Ersatz fOr einen angelassenen Martensit eingesetzt werden kennan,Figure 1. Two designs for the manufacturing of crankshafts by drop forging. Quench and temper (QT) operation (a) requiring expensive straightening and stress relieving cyclesand -as a substitute-continuous cooling (CC) from the forging temperature (b)
In drop forging of parts for the transport industry the classical quench and tempering (QT) of alloyed steels is nowadays substituted by direct continuous cooling (CC) of microalloyed steels with elimination ofquench cracking and expensive straightening and stress relieving cycles. Nevertheless, there are some limitations on strength and toughness achievable by this technique. On two commercial medium carbon (0.3%C) steels microalloyed with vanadium or vanadium and titanium, modified forging parameters and a new two-step cooling (TSC) strategy combined with an additional annealing were applied. Some increase in manufacturing costs, when compared to CC, can be justified by a significant increase in strength and ductility. The improvements attainable through such a modified treatment give evidence of the large potential of multi-phase ferrite-containing microstructures as a substitute ofa tempered martensite. Neuartige Schmiedenachbehandlung von mikrolegierten Stahlen mit mittlerem Kohlenstoffgehalt. Beim Gesenkschmieden von Kraftfahrzeugteilen wird heutzutage die klassische VergOtung (QT) von legierten Stahlen durch eine direkte kontinuierliche AbkOhlung (CC) von mikrolegierten Stahlan ersetzt. Dadurch kennan die RiBbiidungsgefahr eliminiert und das SpannungsarmglOhen und das Richten eingespart werden. Mit dieserTechnologie lassen sich allerdings nicht immer zufriedenstellende Festigkeits-und Zahigkeitseigenschaften erreichen. Auf zwei handelsObliche mit Vanadium oder mit Vanadium und Titan mikrolegierte Stahle mit mittlerem Kohlenstoffgehalt (0,3% C) wurden modifizierte Umformparameter und eine neuartige zweistufige AbkOhlung (TSC) in Kombination mit einem nachtraqllchan GIOhen angewendet. Diese im Vergleich zurCCaUfwendigere Behandlung kann durch eine bemerkenswerte Verbesserung von Festigkeit und Duktilitat gerechtfertigt sein. Die erreichten Ergebnisse verdeutlichen das Potential von mehrphasigen ferrithaltigen GefOgen, die als Ersatz fOr einen angelassenen Martensit eingesetzt werden kennan,Figure 1. Two designs for the manufacturing of crankshafts by drop forging. Quench and temper (QT) operation (a) requiring expensive straightening and stress relieving cyclesand -as a substitute-continuous cooling (CC) from the forging temperature (b)
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.