Compressive Properties of Polyurethane Fiber Mattress Filling Material

2023

In this paper, nanosilver solution was used as an antibacterial agent to prepare antibacterial microcapsules. The mass ratio of the core material to the wall material (Wcore: Wwall), the emulsifier’s hydrophilic–lipophilic balance (HLB) value, the mass ratio of ethanol to the emulsifier in solvent (Wcore: Wemulsion), and the rotational speed (r/min) were used to develop the four-factor, three-level orthogonal experiment, which was meant to investigate the most significant factors and the optimum process preparation parameters impacting the coating rate and yield of microcapsules. It was used to make an antibacterial coating that was applied to the surface paint film of a glass substrate and andoung wood, and it was mixed to the water-based primer with a content of 4%. Analyses of the mechanical, optical, and bactericidal characteristics were conducted. The micromorphology of the nanosilver solution microcapsules is influenced by the emulsifier’s HLB value. The color difference of the antibacterial coating film decreased with increasing emulsifier HLB value; however, the coating film’s gloss remained largely suitable. Additionally, the coating film’s transparency and tensile strength both decreased. It had minimal impact on the paint film’s surface hardness, but the adhesion and tensile strength showed a noticeable downward trend. The surface of the paint film was rough. Escherichia coli and Staphylococcus aureus were resistant to the antibacterial characteristics of the water-based primer film when it was combined with antibacterial nanosilver solution microcapsules by 80.7% and 74.55%, respectively. The coating film’s antibacterial properties were applied to the surface of the andoung wood, which were 75.7% and 71.0%, respectively, and somewhat decreased. In order to successfully inhibit bacteria, the nanosilver solution microcapsules were added to waterborne coatings. This ensures both the outstanding performance of the coating film and the effectiveness of the antibacterial effect. It expands the application prospects of antibacterial microcapsules in coatings.

Section: Resultsmentioning

confidence: 99%

Preparation of Antibacterial Nanosilver Solution Microcapsules and Their Impact on the Performance of Andoung Wood Surface Coating

Pan

2023

“…The solid color-changing compound lasted for 10 min at 25 °C to uniformly heat the discolored compound. When the compound began to change color, the temperature at this time was recorded [ 27 ].…”

Section: Methodsmentioning

confidence: 99%

Preparation of Crystal Violet Lactone Complex and Its Effect on Discoloration of Metal Surface Coating

Zhao

2022

In this paper, a thermochromic complex was prepared from crystal violet lactone (CVL), bisphenol A (BPA) and tetradecanol. The color-changing temperature of the color-changing compound was found to be 25 °C by orthogonal experiment. Microcapsules coated with a thermochromic compound were added into alkyd resin at different mass concentrations. With the increase in temperature and mass fraction of microcapsules in the coating, the color difference of the coating showed an upward trend. The highest variation in the coating’s color difference occurs when there were 10% microcapsules. When the mass fraction of microcapsules was 15.0~25.0%, there was little change to the gloss of the coating. With the increase in the mass fraction of the coating microcapsules, the hardness of the coating gradually increased. The hardness was at its best when the microcapsule concentration was 25%. When the microcapsule concentration was 20%, the impact resistance of the coating was at its best. The coating had good cold-liquid resistance to acetic acid, ethanol, and NaCl solutions, and there was basically no mark on the coating surface before and after the cold-liquid-resistance test. The addition of microcapsules did not change the chemical composition of the coating, and it improved the performance of the coating. When the microcapsule concentration was 10%, the overall performance of the coating was at its best, which laid the technical foundation for thermochromic coating on the metal surface.

“…Adding microcapsules to the water-based coating can improve the toughness of the coating, thus improving the impact resistance of the coating. However, when the amount of microcapsules is too high, it cannot be evenly dispersed in the water-based coating, and the agglomerated microcapsules reduce the impact resistance of the coating [40,41]. A 38 × 19 mm single-sided blade (Shanghai Chengna Trading Co., Ltd., Shanghai, China) was used to draw cracks on the prepared paint film.…”

Section: Effect Of Cip Microcapsules With Different Core-wall Ratios ...mentioning

confidence: 99%

Effects of Shellac Self-Repairing and Carbonyl Iron Powder Microcapsules on the Properties of Dulux Waterborne Coatings on Wood

2023

Magnetic carbonyl iron powder (CIP) microcapsules were created by in situ polymerization using melamine resin as the wall material and CIP as the core material. They were mixed with shellac self-repairing microcapsules to prepare dual-functional wood coatings, and the effect of different amounts of CIP microcapsules in the Dulux Waterborne primer on the performance of the primer was investigated. The findings demonstrated that the core-wall ratio had a significant impact on the characteristics of CIP microcapsules. The microcapsule coating rate reached 57.7% when the core-wall ratio was 0.65:1. The maximum reflection loss of CIP microcapsules with the core-wall ratio of 0.70:1 is −10.53 dB. When the addition amount of shellac self-repairing microcapsules is 4.2%, and the additional amount of CIP microcapsules with a core wall ratio of 0.65:1 and 0.70:1 is 3.0%, the coating color difference is the smallest. The number of microcapsules causes a noticeable drop in the coating’s gloss, and the amount of microcapsules causes a small negative change in the coating’s adherence. With an increase in the number of microcapsules, the coating’s hardness, impact resistance, and tensile resistance first rose and subsequently fell. When the content of CIP microcapsules with core-wall ratio of 0.65:1 and 0.70:1 was 9.0%, the hardness, elongation at break and repair rate of the coating reached the best performance. According to a comprehensive analysis, when the content of CIP microcapsules with core-wall ratio of 0.70:1 is 9.0%, the coating has good performance. At this time, the coating has a color difference of 1.83, a glossiness of 19.3, an adhesion of 2 H, a hardness of 3 H, an impact resistance of 17 kg·cm, and a repair rate of 33.3%. This provides a technical basis for the application of multifunctional coatings on wooden substrates.