An Invitro Analysis of Elemental Release and Cytotoxicity of Recast Nickel–Chromium Dental Casting Alloys

Abstract

Recasting of the casting alloys affects the composition and elemental release which may have cytotoxic effect different from the pure alloy in the surrounding tissues. An Invitro study was conducted to investigate the elemental release and their cytotoxic effects from commercially available Ni-Cr dental casting alloys, commonly used for fabricating fixed partial dentures. Three Ni-Cr alloys [Wiron 99(A), Ceramet (B), and Hi Nickel CB (C)] were tested. Alloy specimens (disks 3 × 5 mm) were casted and grouped as follows: Group I (A(1)/B(1)/C(1)): 100% pure alloy; Group II (A(2)/B(2)/C(2)): 50% new with 50% recast; and Group III (A(3)/B(3)/C(3)): 100% recast. Disks of each alloy type from each group were transferred to Dulbecco's modified eagle medium and left for 3 days at 37°C in an atmosphere of 5% CO(2). Ni, Cr, Co, Cu and Mo elemental release from metal alloys into culture medium was investigated using Inductively Coupled Plasma Mass Spectrometry. Cytotoxicity was tested using mouse fibroblast cells and MTT Assay. Controls consisted of 6 wells containing cells with no alloy specimens. Data were analyzed by two-way analysis of variance followed by t-test. The total amount of elements released in parts per billion for various casting groups were Group I, A(1)-6.572, B(1)-6.732, C(1)-8.407; Group II, A(2)-22.046, B(2)-26.450, C(2)-29.189; Group III, A(3)-84.554, B(3)-88.359, C(3)-92.264. More amounts of elements were released in Hi Nickel CB than Ceramet and Wiron 99 in all the three test groups. Percentage of viable cells from MTT analysis were Group I, A(1)-62.342, B(1)-61.322 C(1)-60.593, Group II, A(2)-58.699, B(2)-56.494, C(2)-52.688, Group III, A(3)-53.101, B(3)-52.195, C(3)-47.586. The viable cells present in the culture media were more in Wiron 99 than Ceramet and Hi Nickel CB. Elemental release increased with amount of recast alloy. Amongst the three alloys tested Hi Nickel CB had significantly higher elements released compared to Ceramet and Wiron 99 in 100% pure alloys, 50% recast and 100% recast alloys. Wiron 99 showed least element release in 100% pure alloy, 50% recast and 100% recast specimens. 100% pure alloys of all three alloys are less cytotoxic, but their cytotoxicity is more on 50% and 100% re-casted alloys. Out of all three variations of casting Wiron 99 was least cytotoxic, followed by Ceramet and Hi Nickel CB. Recasting of alloys significantly increased the elements released and their cytotoxicity.

Antibacterial activity of fig leaf (Ficus carica Linn.) extract against Enterococcus faecalis and its cytotoxicity effects on fibroblast cells

“…The optical density (OD) value of formazan was read by Elisa reader with a wavelength of 620 nm. To assess the percentage of cell viability, the following formula was used [ 20 ].…”

Dental protetik materyallerin biyolojik uyumluluğu ve test yöntemleri

“…Alaşımdaki bakır içe-riğinin ve alaşımların tekrar dökülmesinin sitotoksisite seviyesini arttırdığı, Ni-Cr alaşımlarına göre Co-Cr alaşımların tekrarlayan döküm işleminden daha olumsuz etkilendiği bildirilmiştir. 19 Farklı Ni-Cr alaşımları ile yapılan çalışmalarda, alaşımların tekrarlanan dökümleri sonucunda salınan elementlerin miktarı ve sitotoksisitenin anlamlı derecede arttığı 20 ve mukozal irritasyona 21 neden olabileceği belirtilmektedir.…”

Evaluation of cytotoxicity levels of poly vinyl ether silicone, polyether, and poly vinyl siloxane impression materials: An in vitro study

“…[ 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 ] There are many reports on cytotoxicity, tissue reactions, and hypersensitivity of various other dental materials. [ 26 27 28 ] The potential cytotoxicity of these materials can be tested either by introducing the cells into the material (direct test) or to the eluted extracts of the impression materials (indirect tests). [ 2 ] The assessment of cytotoxicity of these materials is a fundamental step in the evaluation of their biocompatibility.…”