Summary
In this paper, pyromellitic dianhydride (PMDA) was firstly used as fire safety agent for thermoplastic polyurethane (TPU). And, the fire safety improvement of PMDA in TPU was intensively investigated by limiting oxygen index (LOI), smoke density test (SDT), cone calorimeter test, and thermogravimetric/infrared spectroscopy, respectively. It has been found that PMDA could significantly improve the ignition level, and the LOI value increase to 28.5% when 8.0 wt% PMDA was incorporated into TPU; PMDA also could effectively suppress the smoke production and heat release during the combustion process. The peak heat release rate and total smoke release of the sample with 8.0 wt% PMDA were decreased by 68% and 22% compared with pure TPU in cone calorimeter test. The thermogravimetric/infrared spectroscopy results showed that PMDA could improve the thermal stability of TPU composites at high temperature and increased the release of CO2, H2O, and so on. All results confirmed that PMDA would have a good prospect in reducing the fire hazard of TPU.