A Study for the Characteristic Changes Under the Repeated Thermal Exposure in the Process of Repairing Aircraft Sandwich Structures

Abstract

Delamination can be observed in the sound areas during and/or after a couple times exposure to the elevated curing temperature due to the repeated repair condition. This study was conducted for checking the degree of degradation of properties of the cured parts and delamination between skin prepreg and honeycomb core. Specimens with glass honeycomb sandwich construction and glass/epoxy prepreg were prepared. The specimens were cured 1 to 5 times at 260°F in an autoclave and each additionally exposed 50, 100 and 150 hours in the 260°F oven. Each specimen was tested for tensile strength, compressive strength, flatwise tensile strength and interlaminar shear strength. To monitor the characteristics of the resin itself, the cured resin was tested using DMA and DSC. As a results, the decrease of Tg value were observed in the specific specimen which is exposed over 50 hrs at 260°F. This means the change or degradative of resin properties is also related to the decrease of flatwise tensile properties. Accordingly, minimal exposure on the curing temperature is recommended for parts in order to prevent the delation and maintain the better condition.