A polymer with a copoly(ether‐ester‐amidic) structure. II. Laboratory spinning‐drawing operations and fibre characterization

Abstract

ACIERNO, CIAPERONI et al. : A polymer with a copoly(ether-ester-amidic) structure. I1 Actr Polymcrics 37 (1986) Nr. 6 351 PE are independent components in t h e blend a n d that transformations of their supermolecular structures after annealing takes place in t h e way characteristic for pure components. dnnealing of t h e blends at higher temperat u r e (over 413 K) results in a gradual melting of PE. For such films t h e peak attributed t o PE decreases with annealing time t o complete disappearance. I n films of high Moskovskij inkenerno-stroitel'nyj institut im. V. V. Kujbygeva, Moskva, SSSR *) TadZikskij gosudarstvennyj universitet im. V. I. Lenina, Duganbe, SSSR In dunnen Poly(methylmethacry1at)-Filmen wird ein diskretes Spektrum von Festigkeits-, Dehnungsund Lebensdauerniveaus beobachtet. Diesem Spektrum entsprechen sieben diskrete Abmessungen von Mikrodefekten, die aus Gleichungen der Bruchmechanik berechnet wurden. Die berechneten Werte korrelieren gut mit durch Rontgenstreuung