Influence of polypropylene microfibre (PPMF) dispersion procedure on fresh and hardened rendering mortar properties

Abstract

This study was carried out to evaluate the influence of a polypropylene microfibre (PPMF) dispersion procedure on fresh and hardened state properties of rendering mortars. Specimens prepared with two different PPMF dispersion procedures were evaluated comparatively with reference specimens prepared without adding PPMF. Changes in the fresh properties were monitored using flow table, squeeze flow, and air-entrainment tests. The hardened state was characterized by capillary water absorption, air-permeability, dynamic elastic modulus (E), tensile strength according to the Brazilian test, and porosity by the Archimedes immersion method. Results show that the fresh mortar properties were not affected by dispersion procedure and all hardened mortar properties were statistically similar, except for the dimensional variation of the specimens. The study also shows that adding polypropylene microfibres in a dispersed form was more effective in terms of controlling total drying shrinkage than directly adding fibres to the cementitious matrix (as recommended by the manufacturer) or the reference mortar.

Análise das propriedades físico-mecânicas de argamassas de revestimento com a incorporação de fibras de polipropileno e nylon

“…Argamassas densas tendem a restringir deformações mais intensamente do que argamassas menos densas. Portanto, a porosidade reflete no módulo de elasticidade (estático e dinâmico) das argamassas [49].…”

Bond-slip response of steel fibers after exposure to elevated temperatures: Experimental program and design-oriented constitutive equation

“…At last, water and dry powder were mixed for 90 seconds, following the same 30-30-30 seconds in low-high-low speed. The aforementioned mixing procedure was adopted since it results in better homogenization of materials and microfibers according to Dantas et al [20]. A total of 30 cylindrical specimens with a diameter of 50 mm and a height of 100 mm were produced to assess the compressive strength and the dynamic elastic modulus of the material.…”

The effect of fire on pre-cast steel fiber reinforced concrete for tunnel linings: from microstructure to structural simulation.

“…At last, water and dry powder were mixed during 90 seconds, following the same 30-30-30 seconds in low-high-low speed. The aforementioned mixing procedure was adopted since it results in better homogenization of materials and microfibers in mortars [130].…”