Síntese do espinélio MgAl2O4 via "sol-gel"

Heck, A. L.; Taffarel, Sílvio Roberto; Hoffmann, Ronaldo; Jr., U. L. Portugal; Jahn, S. L.; Foletto, Edson Luiz

doi:10.1590/s0366-69132005000200008

Cited by 9 publications

(6 citation statements)

References 5 publications

(5 reference statements)

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…A partir dos difratogramas foram calculados o grau de cristalinidade (Cris) e o tamanho de cristalito (Tc) dos óxidos formados. Diversos trabalhos, principalmente os desenvolvidos na área de catálise, focam em métodos que proporcionam tamanhos de cristalitos cada vez menores, uma vez que estruturas em escala nanométrica podem ser o diferencial em aplicações dessa natureza [1,20,21]. A Tabela I mostra os resultados para cada experimento.…”

Section: Methodsunclassified

Síntese de MgAl2O4 por combustão assistida por micro-ondas: influência dos parâmetros de síntese na formação e na estrutura cristalina

et al. 2016

View full text Add to dashboard Cite

Resumo Nos últimos anos a técnica de combustão assistida por micro-ondas vem recebendo uma atenção especial, por ser uma técnica rápida, de baixo custo e de fácil manuseio, que permite obter materiais com boa homogeneidade química. O aluminato de magnésio (MgAl2O4) é um dos mais bem conhecidos materiais cerâmicos devido às suas excelentes propriedades, como alto ponto de fusão, elevada resistência mecânica em altas temperaturas, boa resistência ao choque térmico e resistência a ácidos e bases. O propósito deste trabalho é avaliar a influência da razão combustível/oxidante (Rco), temperatura de calcinação (Tcal) e da potência do micro-ondas (Pmic) na formação e na estrutura cristalina do MgAl2O4. Para realizar a reação de combustão foram utilizadas três potências (450, 675 e 900 W) e três razões combustível/oxidante (0,8:1, 1:1 e 1,2:1). O material foi calcinado em três temperaturas (700, 800 e 900 ºC) e foram realizadas análises de difração de raios X e microscopia eletrônica por varredura. Um planejamento fatorial 23 foi utilizado para avaliar a influência da Rco, Tcal e Pmic nos parâmetros como a cristalinidade e o tamanho de cristalito. Os resultados mostram que para os MgAl2O4 sintetizados com Rco maiores que 1:1 e Pmic menores que 675 W são obtidos tamanhos de cristalito entre 10 e 20 nm quando calcinados a 700 e 800 ºC. Com relação ao grau de cristalinidade, somente a Tcal exerce uma influência significativa.

show abstract

Section: Methodsunclassified

Síntese de MgAl2O4 por combustão assistida por micro-ondas: influência dos parâmetros de síntese na formação e na estrutura cristalina

et al. 2016

View full text Add to dashboard Cite

show abstract

“…There are several processes to prepare nanocrystalline magnesium aluminate, such as sol-gel [13][14][15][16] , co-precipitation 17 , complexation 1,18 , mechanical milling 3 , mechanical-chemical process 19 , hydrothermal 20 , micro emulsion 21 , combustion method 15,[22][23][24][25][26] and fast pyrolysis 27 . However, many of those are complex, expensive, have several steps, require long time for synthesis, require high temperatures and produce nonhomogeneous and generally low surface area solids 28 .…”

Section: Introductionmentioning

confidence: 99%

Effect of Urea Excess on the Properties of the MgAl2O4 Obtained by Microwave-Assisted Combustion

et al. 2017

View full text Add to dashboard Cite

In this paper, magnesium aluminate spinels were prepared by microwave-assisted combustion, using urea as fuel. In order to evaluate the effect of the urea excess used in the synthesis, its mass was added in a range of 1.0 to 2.5 times the stoichiometric amount required. The materials produced were characterized by TGA, FTIR, XRF, XRD, BET, SEM and TEM. The results demonstrated that magnesium aluminate spinel was formed in all solids, but the crystallinity degree and the specific surface area increased according to the amount of urea that was used in the synthesis. The use of excess fuel in the preparation was therefore advantageous, since it eliminated the need of the calcination step, at high temperatures, in order to stabilize the spinel phase and improve the crystallinity of the solid. The heat generated in the combustion process was sufficient to develop the formation of a nanocrystalline structure and produce high purity materials, with a save of 99.4% in energy.

show abstract

“…1); similar phases were reported in [32]. Magnesium aluminate spinel can in general be obtained either by sol-gel or by microwave-assisted combustion method, since the pure structure of this material is generally obtained when its precursors are calcined above 700 °C; calcination below this temperature leaves aluminum and magnesium hydroxide residues [33]. The advantages of using magnesium aluminate spinel as a catalyst or catalytic support is because it has interesting properties for catalysis such as thermal shock resistance, good mechanical strength at room and high temperatures, low thermal expansion and good catalytic properties [34].…”

Section: Resultsmentioning

confidence: 59%

Nickel catalyst supported on magnesium and zinc aluminates (MgAl2O4 and ZnAl2O4) spinels for dry reforming of methane

et al. 2017

View full text Add to dashboard Cite

Materials such as MgAl 2 O 4 and ZnAl 2 O 4 assessed in the reaction of dry reforming of methane to produce syngas were synthesized by microwave-assisted combustion method using urea as fuel. Samples of synthesized oxides were calcined at 800 °C for 2 h and impregnated with 5% nickel. The impregnated samples were calcined at 850 °C for 4 h to obtain the desired phases. The results of the catalytic tests showed that the catalysts are active for the reaction of dry reforming of methane, and the catalyst that showed the best performance for methane conversion was 5% Ni/MgAl 2 O 4 calcined at 850 °C/4 h. Keywords: chemical synthesis, powder diffraction, oxides, dry reform, nickel catalysts. Resumo Materiais

show abstract

Síntese do espinélio MgAl2O4 via "sol-gel"

Cited by 9 publications

References 5 publications

Síntese de MgAl2O4 por combustão assistida por micro-ondas: influência dos parâmetros de síntese na formação e na estrutura cristalina

Síntese de MgAl2O4 por combustão assistida por micro-ondas: influência dos parâmetros de síntese na formação e na estrutura cristalina

Effect of Urea Excess on the Properties of the MgAl2O4 Obtained by Microwave-Assisted Combustion

Nickel catalyst supported on magnesium and zinc aluminates (MgAl2O4 and ZnAl2O4) spinels for dry reforming of methane

Contact Info

Product

Resources

About