Formação e caracterização óptica de filmes automontados de POMA/PPV

Abstract

Recebido em 5/2/02; aceito em 5/7/02 FORMATION AND OPTICAL CHARACTERIZATION OF POMA/PPV SELF-ASSEMBLY FILMS. A study is presented of the formation and optical properties of polymeric heterostructures from poly(p-phenylene vinylene) (PPV) and poly(o-methoxyaniline) (POMA) produced via the self-assembly technique. POMA layers were obtained in a non self-limiting process from its emeraldine salt, semiconducting form in HCl solution. Thermal conversion of PPV was performed at low temperatures with the substitution of the counter-ion Cl in the PPV precursor by a long sulfonic chain, the dodecylbenzenesulfonate (DBS) ion. The optical properties of PPV films converted in this way are not affected by POMA, which can be used as transparent electrode of PPV luminescent devices.

Estudo da aplicação da poli(o-metoxianilina) e de seus compósitos com negro de fumo no processamento de absorvedores de micro-ondas

“…Ao final desse período, o polímero foi filtrado, Figura 1. Fórmula estrutural da POMA (a) base esmeraldina desprotonada e (b) sal de esmeraldina (protonada) [28] . Figura 2.…”

“…Nesse sentido, a POMA contribui por apresentar melhor solubilidade e interessantes propriedades eletrocrômicas, além de ser facilmente sintetizada via rotas química e eletroquímica [23] . A POMA é um polímero que em um de seus estados de semi-oxidação, base esmeraldina Figura 1a, pode ser protonada quando colocada em meio ácido, assim sua condutividade pode aumentar até 11 ordens de grandeza (1 S.cm -1 ), tornando-se um condutor elétrico [28] . A fórmula estrutural da POMA, em sua forma sal esmeraldina, é esquematizada na Figura 1b [28] .…”

“…A POMA é um polímero que em um de seus estados de semi-oxidação, base esmeraldina Figura 1a, pode ser protonada quando colocada em meio ácido, assim sua condutividade pode aumentar até 11 ordens de grandeza (1 S.cm -1 ), tornando-se um condutor elétrico [28] . A fórmula estrutural da POMA, em sua forma sal esmeraldina, é esquematizada na Figura 1b [28] . A Figura 2 mostra o aspecto morfológico do polímero disponibilizado em literatura, onde se verifica a presença de aglomerados e regiões com textura de flocos [29] .…”

Studies of optical, morphological and electrical properties of POMA/PMMA blends, using two different levels of doping with CSA

“…The optical properties of PANI and its derivatives have also attracted great interest of several research groups. Melo et al [10] showed that the POMA can be used to produce light-emitting heterostructures by self-assembly technique. For the optical characterization of POMA/poly(p-phenylenevinylene) (PPV) films, it was observed that the CP can be used as an optical window for the PPV.…”

Influência da espessura nas propriedades de absorção e emissão e na morfologia de filmes automontados de poli(p-fenileno vinileno

“…Obtendo-se no final de cada ciclo, uma camada dupla (bicamada) que pode ser repetida até se atingir a espessura desejada após a otimização dos parâmetros físicos e quí-micos que envolvem esta técnica. Além de polieletrólitos, é possí-vel também utilizar moléculas iônicas menores 17,21 , tais como o sal de sódio do ácido dodecilbenzenosulfônico (DBS -Figura 1) como poliânion 22 . Neste caso particular não temos a formação específica de uma bicamada, devido ao fato de que o DBS é uma molécula pequena que, além de realizar a troca iônica com o contra-íon Cl, se difunde pela camada do polímero precursor 17 .…”