Thermal Analysis on the Milled Al+B2O3+Si+WO3 System to Synthesize Al2O3-WxSiy-WxBy Powders

Abstract

Composites including silicide of tungsten and boride of tungsten intermetallic compound as reinforced agents in alumina matrix have a good mechanical properties in low and high temperature (high friction resistance, strength, resin stance to creep and relatively high thermal shock resistance), moreover, they have chemical neutral with a high corrosion resistance in a high corrosive and high temperature environment. The purpose of this study is to investigate thermal analysis, phase and microstructural evaluation during synthesis of above mentioned composite by combustion aluminothermic processing in three systems 1-Al+Si+WO 3 , 2-Al+B 2 O 3 +WO 3 and 3-Al+B 2 O 3 +Si+WO 3. A Ball-milled starting material according to stoichiometric ratio was thermal analyzed (DTA-TGA) for each of above mentioned system. The XRD results never show any new phase during ball-milling even up to 10 hours. The forming of tungsten silicide (W x Si y) is in lower temperature in comparison with tungsten boride (W x B y) during the thermal analysis experiments. The presence of Si in the Al+B 2 O 3 +WO 3 system facilitates the formation of tungsten borides. The microstructural observations show a uniform and dense distribution of silicide and boride of tungsten in the alumina matrix. Silicide phases are small grain with spherical morphology whereas; the boride phases are coarser and relatively elongated with irregular morphology.

Study of the Efficiency of the Amino Acid L-Histidine as a Corrosion Inhibitor of 1018 Carbon Steel in Saline Solution Without and with CO2 Saturation

“…The substance's total mass or mass fraction is continuously monitored, and the resulting data is represented on a thermal decomposition curve, commonly referred to as a thermogram. The primary processes measured encompass evaporation, sublimation, decomposition, oxidation, reduction, and gas adsorption 46,49 .…”