요 약 본 연구에서는 투과증발 공정에서 지지체에 따른 투과특성의 차이를 알아보기 위해 고분자 지지체 복합막과 세라믹 지지체 복합막을 제조하였다. 고분자 지지체로는 polyvinylidene fluoride (PVDF)를 사용하였으며 세라믹 지지체로는 a-Al 2 O 3 를 사용하였다. 활성층으로는 각각의 지지체에 고무상 고분자인 polydimethoxysilane (PDMS)를 코팅하였다. 제조한 복합막의 구조와 특성을 살펴보기 위해 SEM, contact angle, XPS로 분석하였으며, 이를 투과증발 공정에 적용 하여 다성분계의 혼합용액에서 복합막의 지지체에 따른 투과 특성을 알아보았다. 투과 증발 실험 결과 세라믹 지지체 복합막의 투과 플럭스는 250.87 g/m 2 h로 고분자 지지체 복합막의 159.64 g/m 2 h 보다 높은 투과 플럭스를 나타내었다. 그러나 선택도의 경우 고분자 지지체 복합막이 31.98로 20.66인 세라믹 지지체 복합막보다 더 높게 나타나는 것을 확 인하였다.Abstract − In this paper, polymer composite membranes and ceramic composite membranes were prepared in order to compare differences in pervaporation performances relative to the support layers. PVDF was used for the polymer support layers, and a-Al 2 O 3 was used for the ceramic support layers. For active layer was coated for PDMS, which is a rubbery polymer. The characterization of membranes were analysed by SEM, contact angle, and XPS. We studied performances relative to the composite membrane support layers in the ABE mixture solutions. The results of the pervaporation, the flux of the ceramic composite membrane was shown to be 250.87 g/m 2 h, which was higher than that of polymer composite membranes, at 195.64 g/m 2 h. However, it was determined that the separation factor of the polymer composite membranes was 31.98 which were higher than that of the ceramic composite membranes, at 20.66.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.