− Until a recent day, degradation of PEMFC (Proton Exchange Membrane Fuel Cells) has been mainly studied in unit cell. But operation and degradation of real PEMFC going along in stack instead of unit cell. Therefore in this work, ADT (Accelerated Degradation Test) of PEMFC was done in stack and the result from stack's test was compared with that of unit cell. The polymer electrolyte membrane was degraded by repeated electrochemical and mechanical degradation method among several ADT methods. Current densities of MEA at 0.6V decreased in stack and unit cell, 28.4% and 27.8% respectively after ADT for 312 hours. Hydrogen crossover current densities of membrane increased in stack and unit cell, 16.8% and 15.2% respectively after ADT for 312 hours. The result of ADT in stack was similar that of ADT in unit cell, which showed that ADT method of unit cell was available to the stack.
Enzyme fuel cells were composed of enzyme anode and PEMFC cathode. Enzyme anodes was fabricated by compression of a mixture of graphite particle, glucose oxidase as a enzyme and ferrocene as a mediator, and then coated with Nafion ionomer. Open circuit voltage (OCV) were measured with variation of anode manufacture factors, to find optimum condition of enzyme anode. Optimum pressure was 9.0 MPar for enzyme anode pressing process. Highest OCV was obtained at 60% graphite composition in enzyme anode. Optimum glucose concentration was 1.7mol/l in anode substrate solution and enzyme activity of anode was stable for 7 days.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.