Structural performance and durability of ultra high performance concrete could demonstrate optimal performance when unity was kept. Accordingly, it is necessary to involve the characteristics and quantitative surface treatment at the same time in order to retain oneness of Ultra-High-Performance Concrete(UHPC) according to construction joint occurrence. Therefore, this study derives a reasonable surface treatment method in a material's point of view through the shear adhesion performance evaluation according to the construction joints surface processing method as a part for securing the adhesion performance of the construction joints when casting UHPC. 180 MPa of required average strength was used for mix of UHPC and surface treatment method was set to totally 7 level that MN, GR-10-0, GR-20-0, GR-30-0, SH-30-5, SH-30-10. After the specimen were manufactured to a size of 150×150×150mm, Direct shear test was performed to evaluate the shear adhesion strength. As a result, it was confirmed that the adhesion performance was improved when executing a surface treatment for the construction joint interface and standard of failure mode of specimen was over Type C. Also, It was considered that interface of cross section and depth of concavo-convex should be concerned.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.