In this study, silicon nitride (SiNx) thin films with different oxygen concentration (i.e., SiON film) were precisely deposited by plasma enhanced atomic layer deposition on Si (100) substrates. Thus, the effect of oxygen concentration on film properties is able to be comparatively studied and various valuable results are obtained. In detail, x-ray reflectivity, x-ray photoelectron spectroscopy, atomic force microscopy, and spectroscopic ellipsometry are used to systematically characterize the microstructural, optical, and electrical properties of SiON film. The experimental results indicate that the surface roughness increases from 0.13 to 0.2 nm as the oxygen concentration decreases. The refractive index of the SiON film reveals an increase from 1.55 to 1.86 with decreasing oxygen concentration. Accordingly, the band-gap energy of these films determined by oxygen 1s-peak analysis decreases from 6.2 to 4.8 eV. Moreover, the I-V tests demonstrate that the film exhibits lower leakage current and better insulation for higher oxygen concentration in film. These results indicate that oxygen affects microstructural, optical, and electrical properties of the prepared SiNx film.
ZnSe nanocrystals have been formed in the silicon dioxide matrix by the sequential high-fluence implantation of Zn + and Se + ions at 500°C. After implantation a part of samples was annealed at 1000°C for 3 min using rapid thermal annealing. Structural and optical properties of ZnSe/SiO 2 nano-composite films were analyzed by means of Rutherford Backscattering Spectrometry, cross-sectional Transmission Electron Microscopy, Raman scattering and photoluminescence techniques. It was shown that a sequence of implantation affects structural and optical properties of synthesized ZnSe clusters. Based on the Raman scattering and photoluminescence data the samples for which Zn ions were implanted first exhibited a better ZnSe crystalline quality than those of reverse sequence of implantation, i.e. with Se ions implanted at the beginning. The bands of blue ZnSe band edge emission and green-red ZnSe deep defect level emission were revealed in the PL spectra of the as-implanted and annealed nano-composites. The PL spectral features observed in the blue region are due to the quantum-size effects in the ZnSe nanocrystals embedded into the silicon dioxide matrix. The PL intensity ratio of the deep defect band to the near edge emission is higher in the samples first implanted with Se ions, and Zn ions implanted next. The effect of rapid thermal annealing on structural and light-emitting properties was discussed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.