The paper investigates aspects of the development of corrosion processes under conditions of moisture condensation in the gas phase in the presence of carbon dioxide, which lead to the formation of local damage. The authors developed and tested a methodology for conducting steels corrosion testing The causes of the formation and the corrosive effect of moisture condensation on steel under conditions of carbon dioxide corrosion at gas production facilities are analyzed. It was found that at elevated temperatures, when the temperature difference is higher, more moisture condenses on the surface of the steel, which leads to an increase in the rate of both general and local corrosion by 2–3 times, compared to room temperature. The increased localization of corrosion processes under conditions of moisture condensation and the presence of CO2 makes the depth index of steel corrosion much higher than the general corrosion rate. When assessing the corrosiveness of environments with condensation of the aqueous phase, the rate of corrosion associated with the depth of the observed corrosion damage should be taken into account. According to the test results, it was determined that samples from the weld compared with the sample from the main body of the pipe differ in the degree of localization of corrosion in conditions of moisture condensation.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.