Ti-substituted barium hexaferrite BaFe 12 O 19 single crystals Ba-Fe 12−x Ti x O 19 with x up to 1.3 and sizes 2−8 mm were grown by spontaneous crystallization from molten sodium carbonate flux. The distribution of Ti on different crystallographic sites was determined from single crystal X-ray diffraction data. For low Ti contents up to x = 0.8 the unit cell expands; on further increase of the Ti amount the unit cell starts to shrink. This behavior for low Ti contents is most likely due to a reduction of Fe 3+ to Fe 2+ for charge balance. At higher Ti concentrations, supposedly vacancies in the transition metal substructure are formed. An increasing Ti concentration results in a monotonous reduction of the Curie temperature from 452 to 251 °C and the saturation magnetization at room temperature from 64.8 to 24.8 emu/g for powder samples and from 70.0 to 60.1 emu/g for single crystals (for x up to 0.78).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.