Powder metallurgy (PM) commercial purity titanium (CP Ti) was fabricated and studied, with an aim of utilization for dental application. PM CP Ti was manufactured using a cost effective approach, where affordable hydrogenation–dehydrogenation (HDH) process Ti 99.4 wt.% powder was consolidated via the following sequence of PM techniques: cold isostatic pressing, warm vacuum pressing at 420 °C and warm direct extrusion at 500 °C. The paper presents the first studies on processing, microstructure, testing of mechanical properties, fatigue performance and bonding strength with different veneer coatings. By employed consolidation process sound material with low porosity (1.5%) and sustained oxygen content (0.21 wt.%) was attained. The tensile properties obtained for PM CP Ti (UTS = 701 MPa, YS0.2 = 512 MPa, ε = 13 %) were improved over to those for cast / milled CP Ti Grade 4 reference, the material commonly used in dentistry. Tested using the ISO 14801 standard for dental implants, the samples machined from PM CP Ti showed fatigue performance similar to CP Ti Grade 4. PM CP Ti used as a metal base material in restoration metal – ceramic systems showed very good bond strength with three commercially available veneering ceramics and complied with the ISO 9693 standard. Within the limitations of this paper, the preliminary results demonstrated that performance of economic PM CP Ti is equal or superior to CP Ti Grade 4 reference material and it can be used in prosthodontics.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.