Defect sites play an essential role in ceria catalysis. In this study, ceria nanocrystals with well-defined surface planes have been synthesized and utilized for studying defect sites with both Raman spectroscopy and O(2) adsorption. Ceria nanorods ({110} + {100}), nanocubes ({100}), and nano-octahedra ({111}) are employed to analyze the quantity and quality of defect sites on different ceria surfaces. On oxidized surfaces, nanorods have the most abundant intrinsic defect sites, followed by nanocubes and nano-octahedra. When reduced, the induced defect sites are more clustered on nanorods than on nanocubes, although similar amounts (based on surface area) of such defect sites are produced on the two surfaces. Very few defect sites can be generated on the nano-octahedra due to the least reducibility. These differences can be rationalized by the crystallographic surface terminations of the ceria nanocrystals. The different defect sites on these nanocrystals lead to the adsorption of different surface dioxygen species. Superoxide on one-electron defect sites and peroxide on two-electron defect sites with different clustering degree are identified on the ceria nanocrystals depending on their morphology. Furthermore, the stability and reactivity of these oxygen species are also found to be surface-dependent, which is of significance for ceria-catalyzed oxidation reactions.

No abstract

Although there are only a few known examples of supported single-atom catalysts, they are unique because they bridge the gap between homogeneous and heterogeneous catalysis. Here, we report the CO oxidation activity of monodisperse single Pt atoms supported on an inert substrate, θ-alumina (Al2O3), in the presence of stoichiometric oxygen. Since CO oxidation on single Pt atoms cannot occur via a conventional Langmuir-Hinshelwood scheme (L-H scheme) which requires at least one Pt-Pt bond, we carried out a first-principles density functional theoretical study of a proposed pathway which is a variation on the conventional L-H scheme and inspired by the organometallic chemistry of platinum. We find that a single supported Pt atom prefers to bond to O2 over CO. CO then bonds with the oxygenated Pt atom and forms a carbonate which dissociates to liberate CO2, leaving an oxygen atom on Pt. Subsequent reaction with another CO molecule regenerates the single-atom catalyst. The energetics of the proposed mechanism suggests that the single Pt atoms will get covered with CO3 unless the temperature is raised to eliminate CO2. We find evidence for CO3 coverage at room temperature supporting the proposed mechanism in an in situ diffuse reflectance infrared study of CO adsorption on the catalyst's supported single atoms. Thus, our results clearly show that supported Pt single atoms are catalytically active and that this catalytic activity can occur without involving the substrate. Characterization by electron microscopy and X-ray absorption studies of the monodisperse Pt/θ-Al2O3 are also presented.

Hydrogen generation from the direct splitting of water by photocatalysis is regarded as a promising and renewable solution for the energy crisis. The key to realize this reaction is to find an efficient and robust photocatalyst that ideally makes use of the energy from sunlight. Recently, due to the attractive properties such as appropriate band structure, ultrahigh specific surface area, and more exposed active sites, two-dimensional (2D) photocatalysts have attracted significant attention for photocatalytic water splitting. This Review attempts to summarize recent progress in the fabrication and applications of 2D photocatalysts including graphene-based photocatalysts, 2D oxides, 2D chalcogenides, 2D carbon nitride, and some other emerging 2D materials for water splitting. The construction strategies and characterization techniques for 2D/2D photocatalysts are summarized. Particular attention has been paid to the role of 2D/2D interfaces in these 2D photocatalysts as the interfaces and heterojunctions are critical for facilitating charge separation and improving photocatalysis efficiency. We also critically discuss their stability as photocatalysts for water splitting. Finally, we highlight the ongoing challenges and opportunities for the future development of 2D photocatalysts in this exciting and still emerging area of research.

The effect of thiolate ligands was explored on the catalysis of CeO2 rod supported Au25(SR)18 (SR = -SCH2CH2Ph) by using CO oxidation as a probe reaction. Reaction kinetic tests, in situ IR and X-ray absorption spectroscopy, and density functional theory (DFT) were employed to understand how the thiolate ligands affect the nature of active sites, activation of CO and O2, and reaction mechanism and kinetics. The intact Au25(SR)18 on the CeO2 rod is found not able to adsorb CO. Only when the thiolate ligands are partially removed, starting from the interface between Au25(SR)18 and CeO2 at temperatures of 423 K and above, can the adsorption of CO be observed by IR. DFT calculations suggest that CO adsorbs favorably on the exposed gold atoms. Accordingly, the CO oxidation light-off temperature shifts to lower temperature. Several types of Au sites are probed by IR of CO adsorption during the ligand removal process. The cationic Au sites (charged between 0 and +1) are found to play the major role for low-temperature CO oxidation. Similar activation energies and reaction rates are found for CO oxidation on differently treated Au25(SR)18/CeO2 rod catalysts, suggesting a simple site-blocking effect of the thiolate ligands in Au nanocluster catalysis. Isotopic labeling experiments clearly indicate that CO oxidation on the Au25(SR)18/CeO2 rod catalyst proceeds predominantly via the redox mechanism where CeO2 activates O2 while CO is activated on the dethiolated gold sites. These results point to a double-edged sword role played by the thiolate ligands on Au25 nanoclusters for CO oxidation.

Vanadia species on aluminas (delta- and gamma-Al2O3) with surface VOx density in the range 0.01-14.2 V/nm2 have been characterized by UV and visible Raman spectroscopy, UV-visible diffuse reflectance spectroscopy (UV-Vis DRS), and temperature-programmed reduction in hydrogen. It is shown that the alumina phase has little influence on the structure and reducibility of surface VOx species under either dehydrated or hydrated conditions. Three similar types of dispersed VOx species, i.e., monovanadates, polyvanadates, and V2O5, are identified on both aluminas under dehydrated conditions. Upon hydration, polymerized VOx species dominate on the surfaces of the two aluminas. The broad Raman band at around 910 cm(-1), observed on dehydrated V/delta-, gamma-Al2O3 at all V loadings (0.01-14.2 V/nm2), is assigned to the interface mode (V-O-Al) instead of the conventionally assigned V-O-V bond. The direct observation of the interface bond is of significance for the understanding of redox catalysis because this bond has been considered to be the key site in oxidation reactions catalyzed by supported vanadia. Two types of frequency shifts of the V=O stretching band (1013-1035 cm(-1)) have been observed in the Raman spectra of V/Al2O3: a shift as a function of surface VOx density and a shift as a function of excitation wavelength. The shift of the V=O band to higher wavenumbers with increasing surface VOx density is due to the change of VOx structure. The V=O stretching band in dispersed vanadia always appears at lower wavenumber in UV Raman spectra than in visible Raman spectra for the same V/Al2O3 sample. This shift is explained by selective resonance enhancement according to the UV-Vis DRS results. It implies that UV Raman has higher sensitivity to isolated and less polymerized VOx species while visible Raman is more sensitive to highly polymerized VOx species and crystalline V2O5. These results show that a multiwavelength excitation approach provides a more complete structural characterization of supported VOx catalysts.

Time-resolved in situ IR was performed during selective catalytic reduction of NO with NH on supported VO-WO/TiO catalysts to examine the distribution and reactivity of surface ammonia species on Lewis and Brønsted acid sites. While both species were found to participate in the SCR reaction, their relative population depends on the coverage of the surface vanadia and tungsta sites, temperature, and moisture. Although the more abundant surface NH intermediates dominate the overall SCR reaction, especially for hydrothermally aged catalysts, the minority surface NH intermediates exhibit a higher specific SCR activity (TOF). The current study serves to resolve the long-standing controversy about the active sites for SCR of NO with NH by supported VO-WO/TiO catalysts.

Ceria has recently shown intriguing hydrogenation reactivity in catalyzing alkyne selectively to alkenes. However, the mechanism of the hydrogenation reaction, especially the activation of H, remains experimentally elusive. In this work, we report the first direct spectroscopy evidence for the presence of both surface and bulk Ce-H species upon H dissociation over ceria via in situ inelastic neutron scattering spectroscopy. Combined with in situ ambient-pressure X-ray photoelectron spectroscopy, IR, and Raman spectroscopic studies, the results together point to a heterolytic dissociation mechanism of H over ceria, leading to either homolytic products (surface OHs) on a close-to-stoichiometric ceria surface or heterolytic products (Ce-H and OH) with the presence of induced oxygen vacancies in ceria. The finding of this work has significant implications for understanding catalysis by ceria in both hydrogenation and redox reactions where hydrogen is involved.